- Lotréne® FD0274 can be easily processed on all types of extruders to make blown or cast films.
- The melt temperature is suggested to be in the range of 150-140 °C.
- The best properties of the blown film are achieved at blow up ratios between 2:1 and 3:1.
- To avoid blocking and shrinkage on the reel, temperature at the nip rolls and take-off should be kept as close as possible to the ambient temperature.
- The recommended thickness range is from 20 um to 100 pm
- Applications
- Thin transparent film
- Thin shrink film
- Foam products
- Food packaging,
- Deep Freeze
- Lamination film
Properties
- Color
- Film Properties
- Polymer Properties
- Properties
The molecular structure of Lotrene® FD0274 makes it possible to produce very thin, clear and glossy films.
(Film properties stated have been obtained using 40 pm blown films lab y test speci produced under ing conditions: 45 mm screw with L/D = 30, die diameter 120 mm, die gap 1.56 mm, BUR 2.5:1).
| Value | Units | Test Method / Conditions | |
| Coefficient Of Friction | 0.12 | - | ASTM D1894 |
| Elongation at Break (MD) | 300.0 | g | ASTM D882 |
| Elongation at Break (TD) | 600.0 | g | ASTM D882 |
| Gloss (45°C) | 59.0 | - | ASTM D2457 |
| Haze | 8.0 | % | ASTM D1003 |
| Impact Strength (F 50) | 110.0 | % | ASTM D1709 |
| Puncture Force | 30.0 | N | Internal Method |
| Tear Resistance (MD) | 65.0 | N/mm | ASTM D 1922 |
| Tear Resistance (TD) | 35.0 | N/mm | ASTM D 1922 |
| Tensile Strength at Break (MD) | 24.0 | MPa | ASTM D882 |
| Tensile Strength at Break (TD) | 22.0 | MPa | ASTM D882 |
| Tensile Strength at Yield (MD) | 11.0 | MPa | ASTM D882 |
| Tensile Strength at Yield (TD) | 11.0 | MPa | ASTM D882 |
| Value | Units | Test Method / Conditions | |
| Crystalline Melting Point | 108.0 | °C | ASTM E794 |
| Density (23°C) | 0.923 | g/cm³ | ASTM D1505 |
| Melt Flow Index | 2.4 | g/10 min | ASTM D1238 |
| Vicat Softening Point | 89.0 | °C | ASTM D1525 |
Regulatory & Compliance
- Certifications & Compliance
- Food Contact & Reach
Lotréne® polyethylene products manufactured by Qatar Petrochemical Company (QAPCO) Q.S.C. comply with US, EU and other food contact legislations. Limitations may apply. All QAPCO Lotréne products are complying with REACH Regulation 1907/2006/EC. The aims of this regulation are to improve the protection of human health and the environment through better and earlier identification of the intrinsic properties of chemical substances. Not suitable for pharmaceutical or medical applications.
Safety & Health
- Safety
Under normal conditions Lotrene® products do not present a toxic hazard through skin contact or inhalation.
Storage & Handling
- Handling & Storage
Polyethylene products should be stored in their original packaging or in clean appropriate silos. The products should be stored in a dry and well-ventilated area and should not be exposed to direct sunlight and/ or heat in any form since this may adversely affect their properties. As a general rule, our products should not be stored for more than three months from receipt date.