Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites Processing Methods
- Applications
- Firefighter Helmets
- Prosthetic Feet
Properties
- Color
- Physical Form
- Cured Properties
- Uncured Properties
Value | Units | Test Method / Conditions | |
Specific Gravity (Net Shape) | 1.89 | g/cc | ASTM D-792 |
Molding Shrinkage (Net Shape) | max. 0.001 (max. 0.001) | inch/inch (mm/mm) | ASTM D-955 |
Flexural Strength (Net Shape) | 72,000 (496) | psi (MPa) | ASTM D-790 |
Flexural Modulus (Net Shape) | 3.1 x106 (21.4) | psi (GPa) | ASTM D-790 |
Tensile Strength (Net Shape) | 41,000 (283) | psi (MPa) | ASTM D-638 |
Tensile Modulus (Net Shape) | 3.4 x106 (23.4) | psi (GPa) | ASTM D-638 |
Izod Impact (notched) (Net Shape) | 32 (1709) | ft.lb./in. (J/M) | ASTM D-256 |
Glass Transition Temperature (Net Shapped) | 260 (127) | °F (°C) Tan Delta | ASTM D-7028 |
Value | Units | Test Method / Conditions | |
Carbon Fiber Content (Nominal) | -63 | %w/w | - |
Resin Content (Nominal) | -37 | %w/w | - |
Fiber Length (Nominal) | 1 | inches | - |
Technical Details & Test Data
- Molding Suggestions
QC 8700 can be molded at temperatures in the range of 260-310°F, with 280°F suggested as a starting point. Cure times will be dependent on molding temperature and part thickness and will typically be 3-5 minutes. Detailed molding suggestions are available on request. Cool molded parts at ambient temperature. A cooling fixture may be needed depending on part thickness and geometry.
Packaging & Availability
- Packaging Type
Storage & Handling
- Shelf Life
- 2 Months (75°F)
- Precautions
QC 8700 contains glass fibers and should be handled carefully in order to minimize skin contact. Molding areas should be well ventilated to minimize exposure to fumes. Presses must be provided with local exhaust to remove vapors from work areas. If adequate ventilation is not available, a respirator approved for removing organic vapor must be used.