Features & Benefits
- Materials Features
- Features
- Good Dimensional Stability
- Good Thermal Stability
- High Impact Resistance
- Impact Copolymer
- Impact Modified
- Low Flow
Applications & Uses
- Markets
- Plastics & Elastomers Processing Methods
- Processing Method
- Extrusion
- Injection Molding
Properties
- Color
- Flame Rating
- Appearance
- Natural Color
- Physical Properties
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Density | 1.24 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3 | g/10 min | ISO 1133 |
Across Flow | 0.95 | % | ISO 294-4 |
Flow | 0.95 | % | ISO 3451 |
Ash Content | 40 | % | - |
Value | Units | Test Method / Conditions | |
Tensile Modulus at 23°C | 1900 | MPa | ISO 527-2/1 |
Tensile Stress Yield at 23°C | 18 | MPa | ISO 527-2/50 |
Tensile Stress Break at 23°C | 16 | MPa | ISO 527-2/50 |
Tensile Strain Yield at 23°C | 3 | % | ISO 527-2/50 |
Tensile Strain Break at 23°C | min. 350 | % | ISO 527-2/50 |
Flexural Modulus 2 (23°C) | 2000 | MPa | ISO 178 |
Flexural Stress (23°C) | 34 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Forms | Granules | - | - |
Charpy Unnotched Impact Strength (23°C) | No Break | - | ISO 179/1eU |
Notched Izod Impact Strength (-40°C) | 4.5 | kJ/m² | ISO 180/1A |
Notched Izod Impact Strength (-20°C) | 6 | kJ/m² | - |
Notched Izod Impact Strength (23°C) | 65 | kJ/m² | - |
Hardness (15 sec) | 70 | Shore D | ISO 868 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (0.45 MPa, Unannealed) | 103 | °C | ISO 75-2/Bf |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 57 | °C | ISO 75-2/Af |
Vicat Softening Temperature | 142 | °C | ISO 306/A50 |
Vicat Softening Temperature | 68 | °C | ISO 306/B50 |
Flame Rating (1.5 mm) | HB | - | UL 94 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 80 to 90 | °C | - |
Drying Time | 3 | hr | - |
Processing (Melt) Temp | 210 to 230 | °C | - |
Mold Temperature | 30 to 40 | °C | - |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Filler / Reinforcement
Calcium Carbonate, 40% Filler by Weight