Properties
- Mechanical Properties
- Physical Properties
- Typical Properties
- Electrical Properties
- Impact Properties
- Flame Characteristics
- Wire Coating Extrusion
- Note
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ¹⁹ Wire and cable - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 12 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 239 | % | ASTM D638 |
| Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ | 210 | MPa | ASTM D790 |
| Hardness (Shore A, 30S reading) ¹¹ | 89 | - | ASTM D2240 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 11 | MPa | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 219 | % | ISO 527 |
| Flexural Modulus (at 12.5 mm/min) ¹¹ | 320 | MPa | ISO 178 |
| Tear Strength ¹¹ | 12 | N/mm | ISO 6383 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.08 | - | ASTM D792 |
| Water Absorption (at 23°C, 48hrs) ¹¹ | 0.16 | % | ASTM D570 |
| Melt Flow Rate (at 250°C, 2.16 kgf) ¹¹ | 6.9 | g/10 min | ASTM D1238 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength (Break) ¹⁹ | 18 | MPa | UL 1581 |
| Tensile Elongation (Break) ¹⁹ | 250 | % | UL 1581 |
| Tensile Strength (Break, after 7days, at 113°C) ¹⁹ | 19 | MPa | UL 1581 |
| Tensile Elongation (Break, after 7days, at 113°C) ¹⁹ | 235 | % | UL 1581 |
| UL Temperature Rating ¹⁹ | 80 | °C | UL 1581 |
| Heat Deformation (at 100°C, 250g) ¹⁹ | 22 | % | UL 1581 |
| VW-1 ¹⁹ | Pass | - | UL 1581 |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity ¹¹ | 5.30E+15 | Ω.cm | IEC 60093 |
| Dielectric Strength (in oil, at 2mm) ¹¹ | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 3.1 | - | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.026 | - | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.017 | - | IEC 60250 |
| Comparative Tracking Index ¹¹ | 600 | V | IEC 60112 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3.6 | - | IEC 60250 |
| Value | Units | Test Method / Conditions | |
| Brittleness Temperature ¹¹ | max. -40 | °C | ASTM D746 |
| Value | Units | Test Method / Conditions | |
| Oxygen Index (LOI) | 26 | % | ISO 4589 |
| Smoke Density (on 0.5mm plaque, Non-Flame, Ds-max) | 69 | - | ASTM E662 |
| Smoke Density (on 0.5mm plaque, Flame, Ds-max) | 117 | - | ASTM E662 |
| Glow Wire Flammability Index (passes at 850°C) | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 3.0 mm) | 850 | °C | IEC 60695-2-13 |
| Value | Units | Test Method / Conditions | |
| Conductor Pre-heat Temperature | 80 - 150 | °C | - |
| Cooling Water Air Gap | 100 - 200 | mm | - |
| Cross-head Temperature | 240 - 260 | °C | - |
| Die Temperature | 240 - 260 | °C | - |
| Drying Temperature | 60 - 80 | °C | - |
| Drying Time | 4 - 6 | Hrs | - |
| Drying Time (Cumulative) | 12 | Hrs | - |
| Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | - | - |
| Feed Zone Temperature | 200 - 240 | °C | - |
| Head Zone Temperature | 240 - 260 | °C | - |
| Maximum Moisture Content | 0.02 | % | - |
| Melt Temperature | 240 - 260 | °C | - |
| Middle Zone Temperatures | 220 - 260 | °C | - |
| Neck Temperature | 240 - 260 | °C | - |
| Screen Pack | 150 - 100 | - | - |
| Screw Speed | 15 - 40 | rpm | - |
| Water Bath Temperature | 15 - 80 | °C | - |