Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Typical Properties
- Electrical Properties
- Impact Properties
- Flame Characteristics
- Wire Coating Extrusion
- Note
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ¹⁹ Wire and cable - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper
Value | Units | Test Method / Conditions | |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 16 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 170 | % | ASTM D638 |
Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ | 160 | MPa | ASTM D790 |
Hardness (Shore A, 30S reading) ¹¹ | 89 | — | ASTM D2240 |
Tensile Stress (Break, 50 mm/min) ¹¹ | 15 | MPa | ISO 527 |
Tensile Strain (Yield, 50 mm/min) ¹¹ | 140 | % | ISO 527 |
Flexural Modulus (at 12.5 mm/min) ¹¹ | 140 | MPa | ISO 178 |
Tear Strength ¹¹ | 7 | N/mm | ISO 6383 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
Melt Flow Rate (at 250°C, 5 kgf) ¹¹ | 20 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Tensile Strength (Break) ¹⁹ | 18 | MPa | UL 1581 |
Tensile Elongation (Break) ¹⁹ | 215 | % | UL 1581 |
Tensile Strength (Break, after 7days, at 113°C) ¹⁹ | 21 | MPa | UL 1581 |
Tensile Elongation (Break, after 7days, at 113°C) ¹⁹ | 160 | % | UL 1581 |
UL Temperature Rating ¹⁹ | 80 | °C | UL 1581 |
Heat Deformation (at 100°C, 250g) ¹⁹ | 9 | % | UL 1581 |
VW-1 ¹⁹ | Pass | — | UL 1581 |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 1.50E+15 | Ω.cm | ASTM D257 |
Surface Resistivity ¹¹ | 5.10E+15 | Ω | ASTM D257 |
Dielectric Strength (in oil, at 2mm) ¹¹ | 24 | kV/mm | IEC 60243-1 |
Relative Permittivity (1 MHz) ¹¹ | 2.9 | — | IEC 60250 |
Dissipation Factor (at at 1 MHz) ¹¹ | 0.04 | — | IEC 60250 |
Comparative Tracking Index ʳ ¹¹ | 600 | V | IEC 60112 |
Value | Units | Test Method / Conditions | |
Brittleness Temperature ¹¹ | max. -40 | °C | ASTM D746 |
Value | Units | Test Method / Conditions | |
UL Recognized (94V-0 Flame Class Rating) ʳ | min. 4 | mm | UL 94 |
Glow Wire Flammability Index (passes at 850°C) ʳ | 3 | mm | IEC 60695-2-12 |
Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 750 | °C | IEC 60695-2-13 |
Oxygen Index (LOI) ʳ | 27 | % | ISO 4589 |
Value | Units | Test Method / Conditions | |
Conductor Pre-heat Temperature | 25 - 120 | °C | — |
Cooling Water Air Gap | 100 - 200 | mm | — |
Cross-head Temperature | 220 - 250 | °C | — |
Die Temperature | 220 - 250 | °C | — |
Drying Temperature | 75 - 85 | °C | — |
Drying Time | 5 - 7 | Hrs | — |
Drying Time (Cumulative) | 12 | Hrs | — |
Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | — | — |
Feed Zone Temperature | 180 - 220 | °C | — |
Head Zone Temperature | 220 - 250 | °C | — |
Maximum Moisture Content | 0.02 | % | — |
Melt Temperature | 220 - 250 | °C | — |
Middle Zone Temperatures | 220 - 250 | °C | — |
Neck Temperature | 220 - 250 | °C | — |
Screen Pack | 150 - 100 | — | — |
Screw Speed | 15 - 85 | rpm | — |
Water Bath Temperature | 15 - 60 | °C | — |