Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Typical Properties
- Electrical Properties
- Flame Characteristics
- Wire Coating Extrusion
- Note
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ¹⁹ Wire and cable - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper
Value | Units | Test Method / Conditions | |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 18 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 180 | % | ASTM D638 |
Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ | 80 | MPa | ASTM D790 |
Hardness (Shore A, 30S reading) ¹¹ | 89 | - | ASTM D2240 |
Tensile Stress (Break, 50 mm/min) ¹¹ | 18 | MPa | ISO 527 |
Tensile Strain (Break, 50 mm/min) ¹¹ | 210 | % | ISO 527 |
Flexural Modulus (at 12.5 mm/min) ¹¹ | 70 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.03 | - | ASTM D792 |
Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 17 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Tensile Strength (Break) ¹⁹ | 2.70E+01 | MPa | UL 1581 |
Tensile Elongation (Break) ¹⁹ | 240 | % | UL 1581 |
Tensile Elongation (Break, after 7days, at 113°C) ¹⁹ | 200 | % | UL 1581 |
Tensile Strength (Break, after 7days, at 136°C) ¹⁹ | 27 | MPa | UL 1581 |
UL Temperature Rating ¹⁹ | 80 | °C | UL 1581 |
Heat Deformation (at 100°C, 250g) ¹⁹ | 4 | % | UL 1581 |
VW-1 ¹⁹ | Pass | - | UL 1581 |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 4.70E+15 | Ω.cm | IEC 60093 |
Comparative Tracking Index ¹¹ | 600 | V | IEC 60112 |
Value | Units | Test Method / Conditions | |
Glow Wire Flammability Index (passes at 960°C) | 3 | mm | IEC 60695-2-12 |
Glow Wire Ignitability Temperature (at 3.0 mm) | 775 | °C | IEC 60695-2-13 |
Value | Units | Test Method / Conditions | |
Conductor Pre-heat Temperature | 25 - 120 | °C | - |
Cooling Water Air Gap | 100 - 200 | mm | - |
Cross-head Temperature | 220 - 250 | °C | - |
Die Temperature | 220 - 250 | °C | - |
Drying Temperature | 75 - 85 | °C | - |
Drying Time | 5 - 7 | Hrs | - |
Drying Time (Cumulative) | 1.20E+01 | Hrs | - |
Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | - | - |
Feed Zone Temperature | 180 - 220 | °C | - |
Head Zone Temperature | 220 - 250 | °C | - |
Maximum Moisture Content | 0.02 | % | - |
Melt Temperature | 220 - 250 | °C | - |
Middle Zone Temperatures | 220 - 250 | °C | - |
Neck Temperature | 220 - 250 | °C | - |
Screen Pack | 150 - 100 | - | - |
Screw Speed | 15 - 85 | rpm | - |