Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Optical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 65 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 110 | % | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 93 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
Hardness (Rockwell M) ¹¹ | 70 | - | ASTM D785 |
Hardness (Rockwell R) ¹¹ | 118 | - | ASTM D785 |
Taber Abrasion (CS-17, 1 kg) ¹¹ | 10 | mg/1000cy | ASTM D1044 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.2 | - | ASTM D792 |
Specific Volume ¹¹ | 0.83 | cm³/g | ASTM D792 |
Density ¹¹ | 1.19 | g/cm³ | ASTM D792 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.15 | % | ASTM D570 |
Water Absorption (at 23°C, saturated) ¹¹ | 0.35 | % | ASTM D570 |
Water Absorption (Equilibrium, at 100°C) ¹¹ | 0.58 | % | ASTM D570 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 7 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (Rate B/50) ¹¹ | 154 | °C | ASTM D1525 |
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 132 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.0000684 | 1/°C | ASTM E831 |
Specific Heat ¹¹ | 1.25 | J/g-°C | ASTM C351 |
Thermal Conductivity ¹¹ | 0.19 | W/m-°C | ASTM C177 |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 1.00E+17 | Ω.cm | ASTM D257 |
Dielectric Strength (in air, at 3.2mm) ¹¹ | 14.9 | kV/mm | ASTM D149 |
Relative Permittivity (50/60 Hz) ¹¹ | 3.17 | - | ASTM D150 |
Relative Permittivity (1 MHz) ¹¹ | 2.96 | - | ASTM D150 |
Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0009 | - | ASTM D150 |
Dissipation Factor (at at 1 MHz) ¹¹ | 0.01 | - | ASTM D150 |
High Voltage Arc Track Rate (PLC) ¹¹ | 2 | PLC Code | UL 746A |
Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
Hot Wire Ignition (PLC 4) ¹¹ | min. 1.5 | mm | UL 746A |
High Ampere Arc Ignition (PLC 1) ¹¹ | min. 3 | mm | UL 746A |
High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
Value | Units | Test Method / Conditions | |
Light Transmission (at 2.54 mm) ¹¹ | 88 | % | ASTM D1003 |
Haze (at 2.54 mm) ¹¹ | 1 | % | ASTM D1003 |
Refractive Index ¹¹ | 1.586 | - | ASTM D542 |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 3204 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 907 | J/m | ASTM D256 |
Tensile Impact Strength (Type S) ¹¹ | 546 | kJ/m² | ASTM D1822 |
Falling Dart Impact (at 23°C) ¹¹ | 169 | J | ASTM D3029 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 120 | °C | - |
Drying Time ⁷ | 3 - 4 | Hrs | - |
Drying Time (Cumulative) ⁷ | 48 | Hrs | - |
Maximum Moisture Content ⁷ | 0.02 | % | - |
Melt Temperature ⁷ | 310 - 330 | °C | - |
Nozzle Temperature ⁷ | 305 - 325 | °C | - |
Front - Zone 3 Temperature ⁷ | 310 - 330 | °C | - |
Middle - Zone 2 Temperature ⁷ | 300 - 320 | °C | - |
Rear - Zone 1 Temperature ⁷ | 290 - 310 | °C | - |
Mold Temperature ⁷ | 80 - 115 | °C | - |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | - |
Screw Speed ⁷ | 40 - 70 | rpm | - |
Shot to Cylinder Size ⁷ | 40 - 60 | % | - |
Vent Depth ⁷ | 0.025 - 0.076 | mm | - |
Value | Units | Test Method / Conditions | |
UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
UV-light (Water exposure/immersion) ᵖ | F1 | - | UL 746C |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability