Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.3 | g/cm³ | ISO 1183 |
Density ¹¹ | 1.3 | g/cm³ | ASTM D792 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ASTM D955 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.47 | % | ISO 294 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.8 - 1 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.93 | % | ISO 294 |
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.1 | % | ASTM D570 |
Wear Factor Washer ¹¹ | 58 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF ¹¹ | 0.41 | — | ASTM D3702 Modified: Manual |
Static COF ¹¹ | 0.45 | — | ASTM D3702 Modified: Manual |
Mold Shrinkage (flow) ᵍ ¹¹ | 0.47 | % | SABIC method |
Mold Shrinkage (xflow) ᵍ ¹¹ | 0.93 | % | SABIC method |
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, 5 mm/min) ¹¹ | 76 | MPa | ISO 527 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 76 | MPa | ISO 527 |
Tensile Strain (Yield, 5 mm/min) ¹¹ | 2.3 | % | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 2.4 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 6830 | MPa | ISO 527 |
Flexural Strength (at 2 mm/min) ¹¹ | 352 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 18200 | MPa | ISO 178 |
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 153 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 153 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 2.8 | % | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.8 | % | ASTM D638 |
Tensile Modulus (at 5 mm/min) ¹¹ | 11030 | MPa | ASTM D638 |
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 98 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 5520 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 182 | °C | ISO 75/Bf |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 166 | °C | ISO 75/Af |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000035 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000342 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000092 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000918 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000035 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000092 | 1/°C | ISO 11359-2 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 182 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 171 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 29 | kJ/m² | ISO 180/1U |
Multi-Axial Impact ¹¹ | 3 | J | ISO 6603 |
Izod Impact (Notched, at 23°C) ¹¹ | 69 | J/m | ASTM D256 |
Izod Impact (Unnotched, at 23°C) ¹¹ | 453 | J/m | ASTM D4812 |
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 15 | J | ASTM D3763 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 80 | °C | — |
Drying Time ⁷ | 4 | Hrs | — |
Maximum Moisture Content ⁷ | 0.15 | % | — |
Melt Temperature ⁷ | 225 - 260 | °C | — |
Front - Zone 3 Temperature ⁷ | 260 - 270 | °C | — |
Middle - Zone 2 Temperature ⁷ | 230 - 245 | °C | — |
Rear - Zone 1 Temperature ⁷ | 200 - 210 | °C | — |
Mold Temperature ⁷ | 45 - 55 | °C | — |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | — |
Screw Speed ⁷ | 30 - 60 | rpm | — |