Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 65 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 3.9 | % | ASTM D638 |
Tensile Modulus (at 5 mm/min) ¹¹ | 4310 | MPa | ASTM D638 |
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 119 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 4380 | MPa | ASTM D790 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 65 | MPa | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 3.8 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 4290 | MPa | ISO 527 |
Flexural Stress ¹¹ | 1.16E+02 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 4240 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.47 | - | ASTM D792 |
Density ¹¹ | 1.46 | g/cm³ | ASTM D792 |
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.03 | % | ASTM D570 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.3 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.5 | % | ASTM D955 |
Wear Factor Washer ¹¹ | 46 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Wear Factor Ring ¹¹ | 0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF ¹¹ | 0.36 | - | ASTM D3702 Modified: Manual |
Static COF ¹¹ | 0.39 | - | ASTM D3702 Modified: Manual |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.05 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 298 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 161 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000041 | 1/°C | ASTM D696 |
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000046 | 1/°C | ASTM D696 |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 247 | °C | ISO 75/Bf |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 154 | °C | ISO 75/Af |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 362 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 44 | J/m | ASTM D256 |
Multi-Axial Impact ¹¹ | 1 | J | ISO 6603 |
Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 5 | J | ASTM D3763 |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 23 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 150 | °C | - |
Drying Time ⁷ | 4 - 6 | Hrs | - |
Front - Zone 3 Temperature ⁷ | 380 - 400 | °C | - |
Middle - Zone 2 Temperature ⁷ | 380 - 400 | °C | - |
Rear - Zone 1 Temperature ⁷ | 370 - 380 | °C | - |
Mold Temperature ⁷ | 175 - 190 | °C | - |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | - |
Screw Speed ⁷ | 60 - 100 | rpm | - |