Features & Benefits
- Materials Features
- Wear and Friction Solutions High Temperature Materials
Design engineer look to replace metal parts and components with thermoplastics whenever possible. Not only can they be produced more cost-effectively, they offer greater design flexibility, weigh less and resist corrosion. The availability of high temperature resins like PEEK, PPS, PPA and PEI can stretch the use of thermoplastic even further.
If you can’t stand the heat… internally lubricated compounds: While auto under-the-hood and industrial machinery might be the first to come to mind, high temperature application are not always driven by hot operating environment. Some application that may never see elevated use temperatures have to survive a hot manufacturing environment (lead-free solder, paint ovens). High temperature generally feature good chemical resistance as well.
Internally lubricated compounds:
The addition of an internal lubricant to a thermoplastic material can improve the wear resistance and can reduce the coefficient of friction in plastic parts. Traditional lubricants like PTFE and PTFE/Si blends are common. Compounds made with high temperature resins can provide wear performance comparable with externally lubricated metal parts.
- Product Features
- FM: 11.2 GPa
- HDT: 255°C
- Good balance of cost and performance
- Low wear and COF
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Break) ¹¹ | 216 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 214 | MPa | ISO 527 |
| Tensile Strain (Break) ¹¹ | 1.2 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 1.6 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 20130 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 324 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 334 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 22700 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 18820 | MPa | ASTM D790 |
| Value | Units | Test Method / Conditions | |
| Density ¹¹ | 1.41 | g/cm³ | ASTM D792 |
| Wear Factor Washer ¹¹ | 16 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.36 | - | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.27 | - | ASTM D3702 Modified: Manual |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 279 | °C | ASTM D648 |
| Value | Units | Test Method / Conditions | |
| Surface Resistivity ¹¹ | 100 - 1000000 | Ω | ASTM D257 |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 939 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 96 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 39 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 120 | °C | - |
| Drying Time ⁷ | 4 | Hrs | - |
| Maximum Moisture Content ⁷ | 0.15 | % | - |
| Melt Temperature ⁷ | 315 - 330 | °C | - |
| Front - Zone 3 Temperature ⁷ | 325 - 340 | °C | - |
| Middle - Zone 2 Temperature ⁷ | 315 - 325 | °C | - |
| Rear - Zone 1 Temperature ⁷ | 310 - 320 | °C | - |
| Mold Temperature ⁷ | 150 - 170 | °C | - |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa | - |
| Screw Speed ⁷ | 30 - 60 | rpm | - |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94HB Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |