Knowde Enhanced TDS
Identification & Functionality
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Break) ¹¹ | 84 | MPa | ASTM D638 |
Tensile Stress (Break) ¹¹ | 86 | MPa | ISO 527 |
Tensile Strain (Break) ¹¹ | 3.4 | % | ISO 527 |
Tensile Strain (Break) ¹¹ | 3.2 | % | ASTM D638 |
Tensile Modulus (at 50 mm/min) ¹¹ | 4750 | MPa | ASTM D638 |
Flexural Stress ¹¹ | 137 | MPa | ISO 178 |
Flexural Stress ¹¹ | 124 | MPa | ASTM D790 |
Flexural Modulus ¹¹ | 4610 | MPa | ASTM D790 |
Flexural Modulus ¹¹ | 5400 | MPa | ISO 178 |
Tensile Modulus (at 1 mm/min) ¹¹ | 5400 | MPa | ISO 527 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.45 | g/cm³ | ISO 1183 |
Density ¹¹ | 1.45 | g/cm³ | ASTM D792 |
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.1 | % | ASTM D570 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.2 | % | ASTM D955 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.16 | % | ISO 294 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.3 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.24 | % | ISO 294 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.35 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 164 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 161 | °C | ASTM D648 |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 161 | °C | ISO 75/Af |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 427 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 48 | J/m | ASTM D256 |
Multi-Axial Impact ¹¹ | 1 | J | ISO 6603 |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 33 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 80 | °C | - |
Drying Time ⁷ | 4 | Hrs | - |
Melt Temperature ⁷ | 200 - 215 | °C | - |
Front - Zone 3 Temperature ⁷ | 210 - 220 | °C | - |
Middle - Zone 2 Temperature ⁷ | 195 - 205 | °C | - |
Rear - Zone 1 Temperature ⁷ | 175 - 190 | °C | - |
Mold Temperature ⁷ | 80 - 110 | °C | - |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | - |
Screw Speed ⁷ | 30 - 60 | rpm | - |
Packaging & Availability
- Country Availability
- Regional Availability