Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 270 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 270 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 1.8 | % | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1.8 | % | ASTM D638 |
Tensile Modulus (at 50 mm/min) ¹¹ | 23510 | MPa | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 366 | MPa | ASTM D790 |
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 366 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 25000 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.45 | g/cm³ | ASTM D792 |
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.03 | % | ASTM D570 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.28 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.75 - 0.85 | % | ASTM D955 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 341 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 327 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 775 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 70 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 150 | °C | - |
Drying Time ⁷ | 4 - 6 | Hrs | - |
Front - Zone 3 Temperature ⁷ | 380 - 400 | °C | - |
Middle - Zone 2 Temperature ⁷ | 380 - 400 | °C | - |
Rear - Zone 1 Temperature ⁷ | 370 - 380 | °C | - |
Mold Temperature ⁷ | 175 - 190 | °C | - |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | - |
Screw Speed ⁷ | 60 - 100 | rpm | - |