LNP THERMOCOMP™ Compound - UX08325 - SABIC's Specialty

Identification & Functionality

Features & Benefits

Materials Features: Cost Effective,
Excellent Dielectric Properties,
Good Mold Release,
High Modulus,
High Stiffness,
High Temperature Resistance,
Surface Mount Technology,
UL Listed,
Very Good Heat Resistance

Applications & Uses

Markets: Automotive & Transportation,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
Interior
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Plastics & Elastomers End Uses: 5G Dipole Antenna,
Automotive Applications,
Automotive Interior Parts,
Cell Phones,
Computer Components,
Consumer Applications,
Containers,
Displays,
Electrical Components,
Electrical/Electronic Applications,
Laptop Antenna,
Mobile Phone Antenna,
Personal Accessories,
Tablets
Plastics & Elastomers Processing Methods: Injection Molding,
Laser Sintering (SLS)

Properties

Flame Rating: UL 94 HB
Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	135	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.8	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	10880	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	197	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	194	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	9770	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	125	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.6	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	11080	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	194	MPa	ISO 178
Flexural Strain (Break, at 2 mm/min) ¹¹	2	%	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	9610	MPa	ISO 178

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	263	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000022	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000054	1/°C	ASTM E831
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	261	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Relative Permittivity (1 GHz) ¹¹	4.2	-	ASTM D150
Dissipation Factor (at at 1 GHz) ¹¹	0.01	-	ASTM D150

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 1.5	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ THERMOCOMP™ Compound UX08325