Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.57 | g/cm³ | ISO 1183 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.06 | % | ISO 62 |
Melt Volume Rate (at 265°C, 1.2 kg) ¹¹ | 12 | cm³/10 min | ISO 1133 |
Melt Volume Rate (at 265°C, 2.16 kg) ¹¹ | 21 | cm³/10 min | ISO 1133 |
Specific Gravity ¹¹ | 1.57 | - | ASTM D792 |
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.01 | % | ASTM D570 |
Mold Shrinkage (flow) ᵍ ¹¹ | 0.21 | % | SABIC method |
Mold Shrinkage (xflow) ᵍ ¹¹ | 1.21 | % | SABIC method |
Value | Units | Test Method / Conditions | |
Tensile Modulus (at 1 mm/min) ¹¹ | 10449 | MPa | ISO 527 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 131 | MPa | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 2.4 | % | ISO 527 |
Flexural Modulus (at 2 mm/min) ¹¹ | 8900 | MPa | ISO 178 |
Flexural Strength (at 2 mm/min) ¹¹ | 184 | MPa | ISO 178 |
Tensile Modulus (at 5 mm/min) ¹¹ | 10330 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 128 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.7 | % | ASTM D638 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 9130 | MPa | ASTM D790 |
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 185 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 222 | °C | ISO 75/Bf |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 205 | °C | ISO 75/Af |
Vicat Softening Temperature (Rate B/50) ¹¹ | 214 | °C | ISO 306 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 213 | °C | ISO 306 |
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000031 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00011 | 1/°C | ISO 11359-2 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 224 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 209 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 43 | kJ/m² | ISO 180/1U |
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 6.9 | kJ/m² | ISO 179/1eA |
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 49 | kJ/m² | ISO 179/1eU |
Izod Impact (Notched, at 23°C) ¹¹ | 55 | J/m | ASTM D256 |
Izod Impact (Unnotched, at 23°C) ¹¹ | 585 | J/m | ASTM D4812 |
Value | Units | Test Method / Conditions | |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | - |
Drying Temperature ⁷ | 120 | °C | - |
Drying Time (Cumulative) ⁷ | 12 | Hrs | - |
Drying Time ⁷ | 2 - 4 | Hrs | - |
Front - Zone 3 Temperature ⁷ | 260 - 270 | °C | - |
Maximum Moisture Content ⁷ | 0.05 | % | - |
Melt Temperature ⁷ | 240 - 265 | °C | - |
Middle - Zone 2 Temperature ⁷ | 245 - 255 | °C | - |
Mold Temperature ⁷ | 65 - 90 | °C | - |
Nozzle Temperature ⁷ | 250 - 260 | °C | - |
Rear - Zone 1 Temperature ⁷ | 220 - 230 | °C | - |
Screw Speed ⁷ | 30 - 60 | rpm | - |