Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Break, 5 mm/min) ¹¹ | 129 | MPa | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 1.8 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 11800 | MPa | ISO 527 |
Flexural Stress (Break, 2 mm/min) ¹¹ | 193 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 11000 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.56 | g/cm³ | ISO 1183 |
Value | Units | Test Method / Conditions | |
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000013 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000054 | 1/°C | ISO 11359-2 |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 275 | °C | ISO 75/Bf |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 235 | °C | ISO 75/Af |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 15 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | - |
Drying Temperature ⁷ | 120 - 150 | °C | - |
Drying Time ⁷ | 4 | Hrs | - |
Front - Zone 3 Temperature ⁷ | 330 - 345 | °C | - |
Middle - Zone 2 Temperature ⁷ | 320 - 330 | °C | - |
Mold Temperature ⁷ | 140 - 165 | °C | - |
Rear - Zone 1 Temperature ⁷ | 305 - 315 | °C | - |
Screw Speed ⁷ | 30 - 60 | rpm | - |
Value | Units | Test Method / Conditions | |
UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |