Knowde Enhanced TDS
Identification & Functionality
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 108 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 108 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.4 | % | ASTM D638 |
Tensile Modulus (at 5 mm/min) ¹¹ | 6260 | MPa | ASTM D638 |
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 170 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 5720 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 12.8 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (Rate B/50) ¹¹ | 175 | °C | ASTM D1525 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 1.64E+02 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 158 | °C | ASTM D648 |
Value | Units | Test Method / Conditions | |
Dielectric Strength (in oil, at 1.6mm) ¹¹ | 33.9 | kV/mm | ASTM D149 |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 512 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 101 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 16 | J | ASTM D3763 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 110 - 120 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 300 - 325 | °C | — |
Nozzle Temperature ⁷ | 300 - 325 | °C | — |
Front - Zone 3 Temperature ⁷ | 290 - 325 | °C | — |
Middle - Zone 2 Temperature ⁷ | 275 - 320 | °C | — |
Rear - Zone 1 Temperature ⁷ | 265 - 315 | °C | — |
Mold Temperature ⁷ | 80 - 110 | °C | — |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
Screw Speed ⁷ | 20 - 100 | rpm | — |
Shot to Cylinder Size ⁷ | 30 - 70 | % | — |
Packaging & Availability
- Regional Availability