Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁵ For detailed processing conditions please contact the SABIC representative. Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Value | Units | Test Method / Conditions | |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 7650 | MPa | ASTM D790 |
Flexural Modulus (at 2 mm/min) ¹¹ | 8440 | MPa | ISO 178 |
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 188 | MPa | ASTM D790 |
Flexural Stress (Break, 2 mm/min) ¹¹ | 200 | MPa | ISO 178 |
Tensile Modulus (at 1 mm/min) ¹¹ | 9475 | MPa | ISO 527 |
Tensile Modulus (at 5 mm/min) ¹¹ | 9425 | MPa | ASTM D638 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 2.4 | % | ISO 527 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 3 | % | ASTM D638 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 131 | MPa | ISO 527 |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 131 | MPa | ASTM D638 |
Value | Units | Test Method / Conditions | |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.06 | % | ISO 62 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.5 | % | SABIC method |
Water Absorption (at 23°C, saturated) ¹¹ | 0.2 | % | ISO 62-1 |
Density ¹¹ | 1.3 | g/cm³ | ISO 1183 |
Melt Flow Rate (at 300°C, 10 kgf) ¹¹ | 30 | g/10 min | ASTM D1238 |
Melt Volume Rate (at 300°C, 10.0 kg) ¹¹ | 26 | cm³/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000018 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000055 | 1/°C | ISO 11359-2 |
Vicat Softening Temperature (Rate A/50) ¹¹ | 164 | °C | ISO 306 |
Vicat Softening Temperature (Rate A/120) ¹¹ | 167 | °C | ISO 306 |
Vicat Softening Temperature (Rate B/50) ¹¹ | 154 | °C | ISO 306 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 156 | °C | ISO 306 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 153 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 147 | °C | ASTM D648 |
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 149 | °C | ISO 75/Ae |
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 155 | °C | ISO 75/Be |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at -30°C) ¹¹ | 85 | J/m | ASTM D256 |
Izod Impact (Notched, at 23°C) ¹¹ | 105 | J/m | ASTM D256 |
Izod Impact (Unnotched, at -30°C) ¹¹ | 550 | J/m | ASTM D4812 |
Izod Impact (Unnotched, at 23°C) ¹¹ | 520 | J/m | ASTM D4812 |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 42 | kJ/m² | ISO 180/1U |
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 45 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 50 | kJ/m² | ISO 179/1eU |
Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 9 | kJ/m² | ISO 179/1eA |
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 45 | kJ/m² | ISO 179/1eU |
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 12 | kJ/m² | ISO 179/1eA |
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁵ | 100 - 120 | °C | - |
Drying Time ⁵ | 2 - 4 | Hrs | - |
Maximum Moisture Content ⁵ | 0.02 | % | - |
Melt Temperature ⁵ | 290 - 330 | °C | - |
Nozzle Temperature ⁵ | 290 - 320 | °C | - |
Front - Zone 3 Temperature ⁵ | 300 - 310 | °C | - |
Middle - Zone 2 Temperature ⁵ | 280 - 300 | °C | - |
Rear - Zone 1 Temperature ⁵ | 270 - 280 | °C | - |
Hopper Temperature ⁵ | 60 - 80 | °C | - |
Mold Temperature ⁵ | 80 - 120 | °C | - |
Value | Units | Test Method / Conditions | |
UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
Glow Wire Ignitability Temperature (at 1.5 mm) ʳ ᵖ | 825 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 3.0 mm) ʳ ᵖ | 800 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index (at 1.5 mm) ʳ ᵖ | 825 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 3 mm) ʳ ᵖ | 775 | °C | IEC 60695-2-12 |