Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 53 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 90 | % | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 81 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2130 | MPa | ASTM D790 |
Hardness (Rockwell R) ¹¹ | 110 | — | ASTM D785 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.12 | — | ASTM D792 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.5 | % | ASTM D570 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 1.2 - 1.3 | % | SABIC method |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 160 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000068 - 0.000079 | 1/°C | ASTM E831 |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 1.00E+16 | Ω.cm | ASTM D257 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at 23°C) ¹¹ | 736 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 95 - 105 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
Maximum Moisture Content ⁷ | 0.07 | % | — |
Minimum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 280 - 305 | °C | — |
Nozzle Temperature ⁷ | 280 - 305 | °C | — |
Front - Zone 3 Temperature ⁷ | 275 - 305 | °C | — |
Middle - Zone 2 Temperature ⁷ | 270 - 305 | °C | — |
Rear - Zone 1 Temperature ⁷ | 265 - 305 | °C | — |
Mold Temperature ⁷ | 75 - 120 | °C | — |
Back Pressure ⁷ | 0.3 - 1.4 | MPa | — |
Screw Speed ⁷ | 20 - 100 | rpm | — |
Shot to Cylinder Size ⁷ | 30 - 50 | % | — |
Vent Depth ⁷ | 0.013 - 0.038 | mm | — |
Packaging & Availability
- Country Availability
- Regional Availability