Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 65 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 55 | % | ASTM D638 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 57 | MPa | ASTM D638 |
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 100 | MPa | ASTM D790 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2550 | MPa | ASTM D790 |
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2450 | MPa | ASTM D790 |
Tensile Modulus (at 50 mm/min) ¹¹ | 2250 | MPa | ASTM D638 |
Flexural Stress (Break, 2.6 mm/min, 100 mm span) ¹¹ | 100 | MPa | ASTM D790 |
Tensile Stress (Yield, 50 mm/min) ¹¹ | 66 | MPa | ISO 527 |
Tensile Strain (Break, 50 mm/min) ¹¹ | 51 | % | ISO 527 |
Flexural Stress (Break, 2 mm/min) ¹¹ | 98 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 2370 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
Melt Flow Rate (at 280°C, 2.16 kgf) ¹¹ | 24 | g/10 min | ASTM D1238 |
Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 65 | g/10 min | ASTM D1238 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.4 - 1.7 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.2 - 1.5 | % | ASTM D955 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 1.99 | % | ISO 62-1 |
Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹ | 0.39 | % | ISO 62-4 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 195 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00009 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000085 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at 60°C to 138°C, flow) ¹¹ | 0.000167 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at 60°C to 138°C, xflow) ¹¹ | 0.000153 | 1/°C | ASTM E831 |
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 181 | °C | ISO 75/Be |
Value | Units | Test Method / Conditions | |
Dielectric Strength (in oil, at 1.6mm) ¹¹ | 22.4 | kV/mm | ASTM D149 |
Dissipation Factor (at at 1 MHz) ¹¹ | 0.017 | — | ASTM D150 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at 23°C) ¹¹ | 211 | J/m | ASTM D256 |
Izod Impact (Notched, at -30°C) ¹¹ | 100 | J/m | ASTM D256 |
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 48 | J | ASTM D3763 |
Instrumented Dart Impact Energy (Peak, at -30°C) ¹¹ | 32 | J | ASTM D3763 |
Izod Impact (Notched, 63.5*12.7*3.2, at 23°C) ¹¹ | 13 | kJ/m² | ISO 180/4A |
Izod Impact (Notched, 63.5*12.7*3.2, at -30°C) ¹¹ | 8 | kJ/m² | ISO 180/4A |
Charpy Impact (Notched, at 23°C) ¹¹ | 21 | kJ/m² | ISO 179/2C |
Charpy Impact (Notched, at -20°C) ¹¹ | 10 | kJ/m² | ISO 179/2C |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 100 - 120 | °C | — |
Drying Temperature ⁷ | 95 - 105 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time ⁷ | 2 - 3 | Hrs | — |
Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
Maximum Moisture Content ⁷ | 0.07 | % | — |
Melt Temperature ⁷ | 280 - 310 | °C | — |
Melt Temperature ⁷ | 270 - 295 | °C | — |
Minimum Moisture Content ⁷ | 0.02 | % | — |
Nozzle Temperature ⁷ | 270 - 300 | °C | — |
Nozzle Temperature ⁷ | 270 - 295 | °C | — |
Front - Zone 3 Temperature ⁷ | 280 - 300 | °C | — |
Front - Zone 3 Temperature ⁷ | 265 - 295 | °C | — |
Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C | — |
Middle - Zone 2 Temperature ⁷ | 260 - 295 | °C | — |
Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C | — |
Rear - Zone 1 Temperature ⁷ | 255 - 295 | °C | — |
Hopper Temperature ⁷ | 60 - 80 | °C | — |
Mold Temperature ⁷ | 80 - 120 | °C | — |
Mold Temperature ⁷ | 65 - 95 | °C | — |
Back Pressure ⁷ | 0.3 - 1.4 | MPa | — |
Screw Speed ⁷ | 20 - 100 | rpm | — |
Shot to Cylinder Size ⁷ | 30 - 50 | % | — |
Vent Depth ⁷ | 0.013 - 0.038 | mm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94HB Flame Class Rating) ᵖ | 1.2 | mm | UL 94 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability