Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Key Characteristics
Low smoke, low toxicity, halogen free, flame retardant thermoplastic compound mainly used in optical fiber cable, data and communication cables. Can also be used in LV power cable insulation and small diameter cable sheathing where high flame retardancy is required.
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Appearance
- Pellets
- Mechanical Properties
- Physical Properties
- Fire & Smoke Properties
Value | Units | Test Method / Conditions | |
Elongation at Break | 180 | % | IEC 60811-501 UL 2556 |
Tensile Strength (at Break) | 12.5 | N/mm² | IEC 60811-501 UL 2556 |
Tensile Strength at Break | 12.5 (1800) | - | - |
Elongation at Break (After Thermal Aging: 7 days at 100°C) | min. 75 (-25) | - | - |
Tensile Strength (After Thermal Aging: 7 days at 100°C) | min. 115 (15) | - | - |
Value | Units | Test Method / Conditions | |
Density | 1.49 | g/cm³ | BS EN ISO 1183-3 ASTM D792 |
Melt Flow Rate (at 150°C / 21.6 kg) | 6 | g/10 min | ASTM D1238 |
Tear Strength (at 40 lb/in) | 7 | N/mm | BS 6469-99.1 |
Value | Units | Test Method / Conditions | |
Halogen Acid Gas Evolution | max. 5 (max. 0.5) | - | - |
Limiting Oxygen Index | 40 | % | BS ISO 4589-2 |
Technical Details & Test Data
- Processing
Extruder - An extruder with an L/D ratio (length/diameter) between 15 and 24 and a screw with a compression ratio 1.2:1 are recommended.
Extruder Temperature Conditions - It is important that the melt temperature is not allowed to rise above 190°C.
As a guide the following temperature profile is recommended:Zone #1 Zone #1 Zone #1 Zone #1 Head Die Celsius 130°C 150°C 170°C 180°C 190°C 190°C Fahrenheit 266°F 302°F 338°F 356°F 374°F 374°F This profile will vary slightly depending on extruder type, head design and output
Screw Water Temperature - Not mandatory, if present we recommend 40°-60°C
Recommended Screen Pack - Spacer ring or breaker plate only
Head & Tool Design - The head and tools should be so designed as to allow streamlined flow of material. To obtain the optimum in physical properties in the case of tubing tools, a maximum draw down ratio of 1.5:1 is recommended to avoid internal stresses.Color Masterbatches: EVA, preferable, and PE based color masterbatches including black, up to a maximum of 1%, have no detrimental effect on the properties. It is recommended that all masterbatches should be thoroughly dried before use for 8 hours at 60°C or 4 hours at 80°C in a de-humidifying drier.
Packaging & Availability
- Packaging Type
- Packaging
the following possibilities are available:
- Moisture resistant sacks containing 25kg
- Gaylord boxes: 1323 lb / 600kg
Storage & Handling
- Storage & Shelf Life
This material has unlimited shelf life. The following storage conditions are recommended:
- Packaging should remain sealed
- Avoid storage outside and in direct sunlight