POLYTHICK 5423A has the following features:
- Exhibits moderate adhesive strength and removability from polypropylene film.
- Displays high transparency and weather resistance because the main component is an acrylate polymer.
- Does not require a curing agent due to its one-component type.
- Easily soluble in various solvents such as ketones solvents, aromatic hydrocarbons solvents and esters solvents.
- Excellent workability due to its low viscosity.
Applications & Uses
- Applications
- Application Method
- Application Methods
1. Preparation of Coating Solution
- This product is generally diluted with a solvent on a ratio of 1:1.
- Use toluene, cyclohexane, ethyl acetate or a combination of these solvents for dilution.
2. Coating
- As for coating machines, a gravure roll coater or another coating machine applicable to low-viscosity coating solutions is suitable.
- The standard coating amount is 5 − 20 g(residue on evaporation)/m2 . However, the optimal amount depends on the application and other conditions.
3. Drying
- Adhesive strength and holding power depends on the amount of coating to be used. However, dry between 50 and 100 °C for 30 − 60 seconds to obtain these desired properties. The coating should be dried very well so that none of the organic solvent remains because this product contains organic solvents.
For detailed information, please refer the Technical Data Sheet.
Properties
- Physical Form
- Odor
- Specific odor
- Physical Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
100% Modulus (3wt % Cross-Linking Agent) | 2.1 | - | - |
Value | Units | Test Method / Conditions | |
Residue on evaporation | approx. 30 | wt % | |
Auto-Ignition Temperature (Ethyl Acetate) | 427 (801) | ℃(°F) | - |
Viscosity at 25°C | approx. 300 | mPa·s | |
Boiling Point (in Ethyl Acetate) | 77 (171) | ℃(°F) | - |
Solvent System | n-hexane : ethyl acetate = Approx. 1 : 1 | wt % | |
Explosive Properties (Ethyl Acetate Lower limit) | 2.2 | vol.% | - |
Explosive Properties (Ethyl acetate Upper limit) | 11.5 | vol.% | - |
Specific Gravity (at 50℃) | 0.98 | - | - |
Flash Point (Tag C.C.) | -25 (-13) | ℃(°F) | - |
Boiling Point (in Water) | 100 (212) | ℃(°F) | - |
Pour Point | Below -10 (14) | ℃(°F) | - |
Residue on Evaporation | approx. 30 | wt % | - |
pH (at 1wt % Aqueous Solution) | approx. 4 | - | - |
pH (at 1wt % Aqueous Solution) | approx. 4.5 | - | - |
Specific Gravity (at 25℃) | 0.83 | - | - |
Viscosity (at 25°C) | 300.0 | mPa・s | - |
Viscosity (at 25°C) | approx. 300 | mPa・s | - |
Tensile strength at Break (Dry Film after Immersion in Water) | 60.0 | - | - |
Technical Details & Test Data
- Performance Tests
The adhesive strength, removability and holding power test results of POLYTHICK 5423A are shown below.
1. Adhesive Strength and Removability
- POLYTHICK 5423A exhibits moderate adhesive strength and removability from polypropylene film.
2. Holding Power
- POLYTHICK 5423A displays high holding power for polypropylene film.
For detailed information, please refer the Technical Data Sheet.