Donglin New Materials - Acrylic impact modifier DL-50

Identification & Functionality

Features & Benefits

Materials Features: Dust-Free,
Good Dispersion,
Good Impact Strength,
Good Thermal Stability,
Good Weather Stability,
High Impact Resistance,
Uniform Distribution
The Advantages Of The Product: 1. Uniform particle size, low dust
2. Good compatibility with PVC resin powder
3. Excellent long-term weather resistance
4. After use, the final product has a small dimensional change rate and good thermal stability
5. Extremely high impact Strength
6. Good dispersion, not easy to agglomerate

Applications & Uses

Markets: Building & Construction,
Consumer Goods
Applications: Building & Construction — Building Envelope & Roofing
Glazing & Window Elements
Building & Construction — Building Materials
Fence, Decks & Rails,
Other Building Materials,
Pipes & Plumbing
Consumer Goods — Housewares
Compatible Polymers & Resins: Polyvinyl Chloride (PVC)
Plastics & Elastomers End Uses: Decking,
Fencing,
Profiles
Product Application: DL-50 is recommended to produce PVC door and window profiles, PVC doors, PVC guardrails and other PVC outdoor products.
Suggested Dosage: Add 4.0-6.0 kg per 100 kg of PVC resin powder (specific treatment for specific products).

Properties

Appearance: Free flowing white powder
Mechanical Properties
Typical Properties
Comparison table of Plasticization and Mechanical Properties of Dl-50 and Similar Foreign Products: Sample/Project DL-50 FM-21 KM-355 IM-808A

Plasticizing time (seconds) 168 160 174 178

Maximum torque (Nm) 36 35.6 35.8 35

Balance torque (Nm) 23.5 23.5 23.6 23.4

Temp @ constant Torque. °C 185 184 185 183

Cantilever rushing in (23℃c condition) 18.6 17.4 18.1 18.9

Cantilever impact (-10°C condition) 11.3 11 11.2 11.5

Tensile Strength 397 393 404 409

Elongation at break 176 160 172 177

Remark
The basic formula of the above data:
100 parts of PVC resin powder (K value 67); 2 parts of organotin stabilizer;7 parts for each of the above impact modifiers; 8 parts for light calcium; internal slip DL- 60 0.5 parts; 0.6 parts of external slip agent.

	Value	Units	Test Method / Conditions
Cantilever Impact (23°C Condition)	min. 15.0	KJ/m2	GB/T1843
Cantilever Impact (-10°C Condition)	min. 15.0	KJ/m2	GB/T1843
Tensile Yield Strength	min. 40.0	Mpa	GB/T1843
Elongation At Break	min. 100.0	%	GB/T1040
Cantilever Burst (After 3000 hours Of Aging Treatment)	min. 12.0	KJ/m2	GB/T1843
Plasticizing Time	160-190	s	-

Packaging & Availability

Storage & Handling

Storage: Product should be stored in a cool and dry environment.

The limited period of the product is tentatively set at 2 years. After the expiration date, it can continue to be used after passing the test.

Shandong Donglin New Materials Acrylic impact modifier DL-50

Sample/Project	DL-50	FM-21	KM-355	IM-808A
Plasticizing time (seconds)	168	160	174	178
Maximum torque (Nm)	36	35.6	35.8	35
Balance torque (Nm)	23.5	23.5	23.6	23.4
Temp @ constant Torque. °C	185	184	185	183
Cantilever rushing in (23℃c condition)	18.6	17.4	18.1	18.9
Cantilever impact (-10°C condition)	11.3	11	11.2	11.5
Tensile Strength	397	393	404	409
Elongation at break	176	160	172	177
Remark	The basic formula of the above data: 100 parts of PVC resin powder (K value 67); 2 parts of organotin stabilizer;7 parts for each of the above impact modifiers; 8 parts for light calcium; internal slip DL- 60 0.5 parts; 0.6 parts of external slip agent.