Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
Properties
- Color
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Injection Molding
| Value | Units | Test Method / Conditions | |
| Elongation at Break (23°C, 1/8” Sample) | 2.0 | % | D638 |
| Haze (2.8mm thick) | 0.35 | % | - |
| Heat Distortion Temperature (Unannealed, 1/2 in, 18.56 kg/cm2 Load Pressure) | 95.0 | °C | D648 |
| Izod Impact Strength (23°C, A method, notched 1/4”×1/2”×5/2”) | 1.6 | kg-cm/cm | D256 |
| Light Transmission (2.8mm thick) | 92.0 | % | D1003 |
| Melt Flow Index (200°C, 5 kg load) | 1.9 | g/10min | D1238 |
| Residual SM monomer | 150.0 | ppm | - |
| Specific Gravity | 1.046 | - | D542 |
| Tensile Strength at Yield (23°C,1/8” Sample) | 560.0 | kg/cm2 | D638 |
| Vicat Softening Temperature (1 kg load, 3 mm Thick ,120 °C/hr ) | 108.0 | °C | D1525 |
| Value | Units | Test Method / Conditions | |
| RTI Elec (1.6 mm) | 50.0 | - | UL 746 |
| RTI Elec (3.2 mm) | 50.0 | - | UL 746 |
| RTI Imp (1.6 mm) | 50.0 | - | UL 746 |
| RTI Imp (3.2 mm) | 50.0 | - | UL 746 |
| RTI Str (1.6 mm) | 50.0 | - | UL 746 |
| RTI Str (3.2 mm) | 50.0 | - | UL 746 |
| Value | Units | Test Method / Conditions | |
| Arc Resistance | PLC 5 | - | ASTM D495 |
| Comparative Tracking Index | PLC 1 | - | UL 746 |
| High Amp Arc lgnition (1.6 mm) | PLC 0 | - | UL 746 |
| High Voltage Arc Tracking Rate | PLC 0 | - | UL 746 |
| Hot-Wire Ignition (1.6 mm) | PLC 4 | - | UL 746 |
| Value | Units | Test Method / Conditions | |
| Flame Rating (1.6 mm, ALL) | HB | - | UL 94 |
| Flame Rating (1.6 mm, ALL) | HB 75 | - | IEC 60695-11-10, -20 |
| Flame Rating (3.2 mm, ALL) | HB | - | UL 94 |
| Flame Rating (3.2 mm, ALL) | HB 40 | - | IEC 60695-11-10,-20 |
| Value | Units | Test Method / Conditions | |
| Back Pressure | 71 - 213 | psi(kgf/cm2) | - |
| Drying Temperature | 80 - 85 | °C | - |
| Drying Time | 2.0 - 4.0 | hr | - |
| Front Zone | 205 - 235 | °C | - |
| Melt Zone | 180 - 190 | °C | - |
| Middle Zone | 195 - 225 | °C | - |
| Mold Temperature | 35 - 70 | °C | - |
| Molding Pressure | Moderate to Moderately High | - | - |
| Molding Speed | Moderate to Fast | - | - |
| Nozzle | 210 - 240 | °C | - |
| Rear Zone | 185 - 210 | °C | - |
| Screw Speed | 30 - 120 | rpm | - |
Regulatory & Compliance
- Certifications & Compliance