Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
- Flammability
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Tensile Stress at Break at +23°C | 90-100 | MPa | ISO 527-2 |
Tensile Modulus at +23°C | 5000-6000 | MPa | ISO 527-2 |
Izod Impact Strength, Notched (+23°C) | 7-9 | kJm2 | ISO 180/A |
Tensile Strain at Break (+23°C) | 3-4 | % | ISO 527-2 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (50 N) | 205 | °C | ISO 306 |
Heat Deflection Temperature (1,80 Mpa) | 195 | °C | ISO 75 |
Melting Temperature (10 K/Min) | 225 | °C | ISO 11357 |
Value | Units | Test Method / Conditions | |
Density | 1.38-1.41 | g/cm3 | ISO 1183 |
Moisture Content | max. 0.1 | % | ISO 15512 |
Molding Shrinkage (Normal) | 1.1 | % | ISO 294-4 |
Molding Shrinkage (Parallel) | 0.5 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Volume Resistivity | 10000000000000000 | Ohm.cm | IEC 60093 |
Surface Resistivity | 1.00E+14 | Ohm | IEC 60093 |
Value | Units | Test Method / Conditions | |
Flame Rating (0,75 mm) | HB | - | UL 94 |
Flame Rating (1,6 mm) | HB | - | UL 94 |
Value | Units | Test Method / Conditions | |
Predrying Temperature | 100-120 | °C | - |
Predrying Time | 4-8 | hours | - |
Melting Temperature | 250-270 | °C | - |
Nozzle Temperature | 240-260 | °C | - |
Pre-3 Region Temperature | 240-260 | °C | - |
Mid-2 Region Temperature | 230-250 | °C | - |
Aft-1 Region Temperature | 230-240 | °C | - |
Mold Temperature | 80-100 | °C | - |
Hold Pressure | 40-80 | MPa | - |