Properties
- Film Properties (PA Monolayer - Airblown Films)
Value | Units | Test Method / Conditions | |
Melting Point | 182 - 186 | °C | ISO 11357-3 |
Crystallization Temperature (Tc) | 135 - 139 | °C | ISO 11357-3 |
Glass Transition Temperature (Tg) | 29 - 33 | °C | ISO 11357-3 |
Haze | 21 - 23 | % | ASTM D-1003 |
Gloss (at 60°) | 75 - 95 | % | ASTM D-523 |
Oxygen (T=23°C, RH=0%) | 94 - 96 | ml/m2.day | ASTM D-3985 |
Water Vapor (T=40°C, RH=90%) | 110 - 130 | g/m2.day | JIS Z-0208 |
Coefficient of Friction (Static) | 0.74 - 0.78 | - | ASTM D-1894 |
Coefficient of Friction (Dynamic) | 0.74 - 0.78 | - | ASTM D-1894 |
Tensile Strength at Break | 90 - 110 | Mpa | ISO 527-3 |
Tensile Elongation at Break | 480 - 500 | % | ISO 527-3 |
Tensile Modulus | 300 - 400 | Mpa | ISO 527-3 |
Tear Load | 5.0 - 5.2 | N | ASTM D1922 |
Puncture Energy | 25 - 27 | mJ | JAS P-1019 |
Puncture Deformation | 10 - 11 | mm | JAS P-1019 |
Spencer Impact Energy | 900 - 1000 | mJ | ASTM D3420 |
Flex Crack (Gelboflex) (at 23°C 1000 Cycles) | 0 | Holes/0,04m2 | Mil B-131C |
Flex Crack (Gelboflex) (at 5°C 100 Cycles) | 0 | Holes/0,04m2 | Mil B-131C |
Technical Details & Test Data
- Notes
- Equipment: 5 layers airblown line.
- Die: Diameter = 90 mm • Gap = 1,4 mm.
- Structure: PE (outer) / PE / PA (medium) / PE / PE (inner) •
- PA layer delaminated for the tests.
- Layer thickness distribution: PE = 50μm, PA = 50μm,
- PE = 50μm (Total film thickness = 150μm).
- Cooling conditions: Chiller temp. = 13ºC • Take off rolls = 35ºC.
- Film orientation: Blow-up ratio = 2,1 •
- Take-off speed = 6m min-1.
- Samples conditioning and testing conditions: T = 23ºC, RH = 50%.
- Applications
Plasticized, impact modified and heat stabilized PA6/6.6/12 grade.