ELASTOSIL® P 7671 A/B can be used for flexible molding applications in prosthetics.
Processing
The components A and B of ELASTOSIL® P 7671 A/B are mixed homogeneously in a ratio of 1 : 1 and vulcanize rapidly at temperatures over 100°C. In a given application the required curing conditions (temperature and time) will also depend on the size and thickness of the part.
- Important note: The platinum catalyst is in component A.
- Caution: Only A and B components with the same batch number may be processed together.
Properties
- Catalyst Properties
- Cured Properties
- Uncured Properties
- Properties
- Low viscosity, pourable
- Short pot-life
- Rapid cure at room temperature which can be accelerated considerably by the application of heat.
Value | Units | Test Method / Conditions | |
Mix Ratio (A:B) | 1:1 | parts by weight | - |
Pot Life (A+B, at 23°C) | 40 | minutes | DIN EN ISO 2555 |
Value | Units | Test Method / Conditions | |
Elongation (at break) | 400 | % | ISO 37 Type 1 |
Shore Hardness 00 | 18 | - | ASTM D 2240 |
Tear Strength | 1.5 | N/mm | ASTM D 624 B |
Tensile Strength | 0.5 | N/mm² | ISO 37 Type 1 |
Value | Units | Test Method / Conditions | |
Density (at 23°C, Componenet A) | 1.01 | g/cm³ | DIN EN ISO 2811-1 |
Density (at 23°C, Componenet B) | 1.05 | g/cm³ | DIN EN ISO 2811-1 |
Dynamic Viscosity (Component A) | 1800 | mPa·s | DIN EN ISO 3219 |
Dynamic Viscosity (Component B) | 1800 | mPa·s | DIN EN ISO 3219 |