Properties
- Flame Rating
- Flame Rating
- UL 94 V0
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength - at Break (5 mm/min, 23°C) | 120 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 150°C) | 70 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 60°C) | 110 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 90°C) | 100 | MPa | ISO 527 |
Tensile Strength - at Break (5 mm/min, 120°C) | 85 | MPa | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 150°C) | 5 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 23°C) | 1.3 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 60°C) | 1.5 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 90°C) | 2 | % | ISO 527 |
Tensile Elongation - at Break (5 mm/min, 120°C) | 4 | % | ISO 527 |
Elastic Modulus (Tensile Speed - 1 mm/min, 23°C) | 13000 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 60°C) | 11500 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 90°C) | 9000 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 120°C) | 7500 | MPa | ISO 527 |
Elastic Modulus Tensile Speed ( 1 mm/min, at 150°C) | 5000 | MPa | ISO 527 |
Charpy Unnotched Impact Strength ( +23°C) | 30 | kJ/m2 | ISO 179-1eU |
Charpy Notched Impact Strength (+23°C) | 6 | kJ/m2 | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Moisture Absorption (Air, After 24Hrs) | 0.22 | % | ISO 62-4 |
Linear Shrinkage at Moulding - Longitudinal (2.0mm/60Mpa) | 0.35÷0.50 | % | ISO 294-4 |
Linear Shrinkage at Moulding - Transversal (2.0mm/60Mpa)) | 0.70÷1.00 | % | ISO 294-4 |
Density | 1.49 | g/cm3 | ISO 1183/A |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (1.81 mn/m2) | 260 | °C | ISO 75 |
Heat Deflection Temperature - HDT (0.45 mn/m2) | 290 | °C | ISO 75 |
Vicat Softening Point - VST (50 N, eating Rate 50°C/H) | 260 | °C | ISO 306 |
Coefficient of Linear Thermal Expansion - CLTE - (Longitudinal, +30°C to +100°C) | 15 | μm/(m·°C) | ISO 11359-2 |
Continuous Use Temperature - C.U.T (Long Period, 20,000H) | 140 | °C | ASTM E1641/E1877 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index - CTI (Solution A , Without Surfactant)) | 600 | V | IEC 60112 |
Surface Resistivity | 1E+12 | ohm | IEC 60093 |
Value | Units | Test Method / Conditions | |
Flammability Rating (3.00 mm Thickness) | V-0 | - | UL 94 |
Flammability Rating (1.50 mm Thickness) | V-0 | - | UL 94 |
Flammability Rating (0.75 mm Thickness) | V-0 | - | UL 94 |
Glow Wire Flammability Index - GWFI | 960/1 | - | IEC60695-2-12 |
Glow Wire Ignition Test - GWIT | 775/1 | °C/mm | IEC 60695-2-13 |