Knowde Enhanced TDS
Identification & Functionality
- Backing Material Type
- Chemical Family
- Technologies
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Features
- Low VOC –JIS A-1901
- Low FOG - VDA278
- Aggressive acrylic adhesive
- Good shear properties
- Moisture stable PCK liner
- Benefits
- Acid free, PH Neutral
- Non-outgassing and non-migratory
- Smooth adhesive profile
- Excellent adhesion to a wide variety of surfaces.
- Chemical & UV resistant
- Excellent handling and die-cutting.
- Non-corrosive & non-oxidizing
Applications & Uses
- Applications
- Compatible Substrates & Surfaces
- Applications
- Insulation and Shielding
- Wire harnessing
- Foam bonding applications
- Interior applications that require low vOC and low FOG characteristics
- Flexible Printed Circuits
- Printed Circuit Boards
- Archiving, photo mounting
- Application Details
For best performance surfaces must be clean, dry and free of any oil, grease or other contaminant.
Properties
- Physical Properties
| Value | Units | Test Method / Conditions | |
| Total Thickness | 8.7 | mils | — |
| Loop Tack (stainless steel) | 6.4 | lbs./in. | PSTC-16-Method A |
| Peel Adhesion (180° 2 mil PET Backed 30minute dwell, stainless steel) | 8.5 | lbs./in. | PSTC-101-Method A |
| Peel Adhesion (180° 2 mil PET Backed 24hours dwell, stainless steel) | 9.9 | lbs./in. | PSTC-101-Method A |
| Peel Adhesion (180° 2 mil PET Backed 30minute dwell, ABS) | 7.9 | lbs./in. | PSTC-101-Method A |
| Peel Adhesion (180° 2 mil PET Backed 30minute dwell, Polycarbonate) | 8.3 | lbs./in. | PSTC-101-Method A |
| Peel Adhesion (180° 2 mil PET Backed 30minute dwell, HDPE) | 2.3 | lbs./in. | PSTC-101-Method A |
| Peel Adhesion (180° 2 mil dead soft aluminum foil, 30minute dwell, stainless steel) | 9.0 | lbs./in. | PSTC-101-Method A |
| Peel Adhesion (180° 2 mil dead soft aluminum foil, 30minute dwell, Polypropylene) | 2.5 | lbs./in. | PSTC-101-Method A |
| Shear (1 kg weight, 72°F) | min. 85 | hours | PSTC-107-Method A |
| Shear (5 kg weight, 72°F) | 6.0 | hours | PSTC-107-Method A |
| Tensile (MD/CD) | 10.0 | lbs./in. | ASTM-D822 |
| Elongation (MD) | 100.0 | % | ASTM-D822 |
| Formaldehyde Content | 0.4 | µ g/m3 | JIS-A 1801 |
| Acetaldehyde Content | 1.2 | µ g/m3 | JIS-A 1801 |
| Xylenes Content | 1.4 | µ g/m3 | JIS-A 1801 |
| Fog | 30.0 | µg/g | VDA278 |
| Fog | 0.11 | mg | SAE J1756 |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
- Certifications
- JIS A-1901
- ISO 18916
Technical Details & Test Data
- Product Construction
- Carrier: 0.5 mil PET
- Adhesive: 1.2 mils LV820 LOW VOC Acrylic
- Liner: 80# Natural PCK or 72# White PCK
- Web Width: 54”
- Service Temperature
- Application : Above 50°F (10°C) for best performance
- End Use : -40°F to 300°F (-40°C to 121°C) depending on laminate construction and end use application
- Foam Bonding Performance
Substrate Application Method Result EPDM Room Temp with 50% compression Foam Destruction
Nitrile PVCc Room Temp with 50% compression Foam Destruction
EVA Blend Room Temp with 50% compression Foam Destruction
Polyether polyurethane Foam Room Temp with 50% compression Foam Destruction
NBR-PVC Room Temp with 50% compression Foam Destruction
Storage & Handling
- Shelf Life
Two year shelf life when stored at 75°F. (24°C.) and 50% relative humidity or less. It is recommended that the product be stored in its original package until ready to use.