SLOVAMID 66 GF 20 GB 10 HI

Identification & Functionality

Additives Included

Impact Modifier

Chemical Family

Polyamides

Fillers Included

Glass Bead,

Glass Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Impact Modified

Applications & Uses

Markets

Building & Construction,

Consumer Goods

Applications

Building & Construction — Building Materials

Other Building Materials

Consumer Goods — Footwear

Consumer Goods — Other Consumer Goods Applications

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Building Materials,

Footwear,

Safety Helmets,

Sporting Goods

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength	145	MPa	ASTM D 638
Tensile Modulus	7300	MPa	ISO 527
Flexural Strength	145	MPa	ASTM D 790
Flexural Modulus	5750	MPa	ISO 178
Charpy Notched Impact Strength (23°C)	18	kJ/m2	ISO 179/1eA
Charpy Notched Impact Strength (-20°C)	12	kJ/m2	ISO 179
Charpy Impact Strength (23°C)	90	kJ/m2	STN EN ISO 179
Charpy Impact Strength (-20°C)	75	kJ/m2	STN EN ISO 179
Elongation	3	%	ASTM D638

Physical Properties

	Value	Units	Test Method / Conditions
Melt Mass Flow Rate - MFR (275°C/0.325 kg)	2	g/10 min	STN EN ISO 1133
Density	1.38	g/cm3	ISO 1183/A
Water Content	0.15	%	STN EN ISO 3344

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT	202	°C	STN EN ISO 75-2 (A)
Melting Temperature (DSC)	260	°C	STN EN ISO 11357-1
Vicat Softening Temperature (B)	195	°C	STN EN ISO 306

Processing Parameters

	Value	Units	Test Method / Conditions
Mold Temperature Range	60 - 80	°C	--
Drying: Temperature/Time	80/4	°C/h	--
Manufacturing Shrinkage - length/width	1.12/0.98	%	STN EN ISO 294-4
Injection Pressure	70 - 120	MPa	--
Melt Temperature Range	280 - 300	°C	--