Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.71 | g/cm³ | ASTM D1895 |
Arc Resistance | 185 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 579 | V | ASTM D3638 |
Compressive Strength | 152 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 180 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.5 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.067 | — | ASTM D150 |
Flexural Modulus | 10147 | MPa | ASTM D790 |
Flexural Strength | 94.4 | MPa | ASTM D790 |
Heat Resistance | 142 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 84 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.3 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 17 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0067 | m/m | ASTM D6289 |
Oxygen Index | 35.7 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.9 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.89 | % | ASTM D6289 |
Rockwell Hardness | 72 | E-Scale | ASTM D785 |
Specific Gravity | 1.66 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 11480 | MPa | ASTM D638 |
Tensile Strength | 61 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 4300000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.27 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.7 | g/cm³ | ASTM D1895 |
Arc Resistance | 186 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 422 | V | ASTM D3638 |
Compressive Strength | 167 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 194 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.6 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.047 | — | ASTM D150 |
Flexural Modulus | 11158 | MPa | ASTM D790 |
Flexural Strength | 84.5 | MPa | ASTM D790 |
Heat Resistance | 155 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 96 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.8 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 21.8 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0036 | m/m | ASTM D6289 |
Oxygen Index | 35.7 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.62 | % | ASTM D6289 |
Rockwell Hardness | 74 | E-Scale | ASTM D785 |
Specific Gravity | 1.67 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 13348 | MPa | ASTM D638 |
Tensile Strength | 59 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 75000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.22 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.7 | g/cm³ | ASTM D1895 |
Arc Resistance | 186 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 467 | V | ASTM D3638 |
Compressive Strength | 164 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 202 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.062 | — | ASTM D150 |
Flexural Modulus | 9803 | MPa | ASTM D790 |
Flexural Strength | 97.2 | MPa | ASTM D790 |
Heat Resistance | 152 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 81 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.2 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0055 | m/m | ASTM D6289 |
Oxygen Index | 35.7 | % | ASTM D2863 |
Permittivity (at 1MHz) | 7 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.69 | % | ASTM D6289 |
Rockwell Hardness | 76 | E-Scale | ASTM D785 |
Specific Gravity | 1.67 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 11785 | MPa | ASTM D638 |
Tensile Strength | 57 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 100000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.28 | % | ASTM D570 |