Plastics Engineering Company 04311 Two-stage Phenolic

Identification & Functionality

Chemical Family: Phenol Formaldehyde (PF),
Phenols & Phenolics
Polymer Name: Phenol Formaldehyde (PF)
Reinforcement Material: Mineral
Composite Materials Functions: Molding Compound
Technologies: Composite Materials
Product Families: Composite Materials — Prepregs & Molding Compounds
Other Prepregs & Molding Compounds

Features & Benefits

Materials Features: Arc Resistant,
Cost Effective,
Dimensional Stability,
Excellent Mechanical Strength,
Excellent Track Resistance Properties,
Good Mechanical Properties,
Good Processability,
Heat Resistance,
High Temperature Strength,
Pourable,
Two-Stage,
UL Listed

Applications & Uses

Markets: Consumer Goods,
Electrical & Electronics
Applications: Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
Consumer Electronics
Consumer Goods — Housewares
Electrical & Electronics — Parts & Components
Connectors,
Housings & Enclosures,
Terminal Blocks, Plugs & Sockets
Composites End Use: Cases,
Home Appliances,
Housings
Composites Processing Methods: Compression Molding,
Injection Molding
Plastics & Elastomers Processing Methods: Transfer Molding

Properties

	Value	Units	Test Method / Conditions
Apparent Density	0.71	g/cm³	ASTM D1895
Arc Resistance	154	sec	ASTM D495
Coefficient of Thermal Expansion	5.9e-05	per °C	ASTM E831
Comparative Tracking Index	177	V	ASTM D3638
Compressive Strength	176	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	168	°C	ASTM D648
Dielectric Strength (Short Time)	10.9	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.063	—	ASTM D150
Flexural Modulus	8205	MPa	ASTM D790
Flexural Strength	89.6	MPa	ASTM D790
Heat Resistance	206	°C	ASTM D794
Impact Strength (Drop Ball)	89	J/m	Plenco
Impact Strength (Notched, Izod)	16	J/m	ASTM D256
Impact Strength (Notched, Charpy)	16.6	J/m	ASTM D256
Mold Shrinkage *	0.0082	m/m	ASTM D6289
Oxygen Index	28.1	%	ASTM D2863
Permittivity (at 1MHz)	5.2	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.29	%	ASTM D6289
Rockwell Hardness	79	E-Scale	ASTM D785
Specific Gravity	1.48	—	ASTM D792
Tensile Elongation	0.8	%	ASTM D638
Tensile Modulus	9173	MPa	ASTM D638
Tensile Strength	57	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.49	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-1	—	UL 94
Volume Resistivity	400000000000	ohm·cm	ASTM D257
Water Absorption	0.27	%	ASTM D570

	Value	Units	Test Method / Conditions
Apparent Density	0.72	g/cm³	ASTM D1895
Arc Resistance	153	sec	ASTM D495
Coefficient of Thermal Expansion	5.9e-05	per °C	ASTM E831
Comparative Tracking Index	175	V	ASTM D3638
Compressive Strength	182	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	186	°C	ASTM D648
Dielectric Strength (Short Time)	13.4	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.052	—	ASTM D150
Flexural Modulus	9569	MPa	ASTM D790
Flexural Strength	79.5	MPa	ASTM D790
Heat Resistance	204	°C	ASTM D794
Impact Strength (Drop Ball)	87	J/m	Plenco
Impact Strength (Notched, Izod)	16.9	J/m	ASTM D256
Impact Strength (Notched, Charpy)	19.9	J/m	ASTM D256
Mold Shrinkage *	0.0035	m/m	ASTM D6289
Oxygen Index	28.1	%	ASTM D2863
Permittivity (at 1MHz)	5.1	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.22	%	ASTM D6289
Rockwell Hardness	83	E-Scale	ASTM D785
Specific Gravity	1.49	—	ASTM D792
Tensile Elongation	0.7	%	ASTM D638
Tensile Modulus	9791	MPa	ASTM D638
Tensile Strength	56	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.49	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-1	—	UL 94
Volume Resistivity	4900000000000	ohm·cm	ASTM D257
Water Absorption	0.29	%	ASTM D570

	Value	Units	Test Method / Conditions
Apparent Density	0.69	g/cm³	ASTM D1895
Arc Resistance	147	sec	ASTM D495
Coefficient of Thermal Expansion	5.9e-05	per °C	ASTM E831
Comparative Tracking Index	175	V	ASTM D3638
Compressive Strength	198	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	190	°C	ASTM D648
Dielectric Strength (Short Time)	10.9	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.06	—	ASTM D150
Flexural Modulus	8924	MPa	ASTM D790
Flexural Strength	96	MPa	ASTM D790
Heat Resistance	206	°C	ASTM D794
Impact Strength (Drop Ball)	89	J/m	Plenco
Impact Strength (Notched, Izod)	16.9	J/m	ASTM D256
Impact Strength (Notched, Charpy)	19.7	J/m	ASTM D256
Mold Shrinkage *	0.005	m/m	ASTM D6289
Oxygen Index	28.1	%	ASTM D2863
Permittivity (at 1MHz)	5.7	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.22	%	ASTM D6289
Rockwell Hardness	86	E-Scale	ASTM D785
Specific Gravity	1.47	—	ASTM D792
Tensile Elongation	0.7	%	ASTM D638
Tensile Modulus	9184	MPa	ASTM D638
Tensile Strength	57	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.49	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-1	—	UL 94
Volume Resistivity	390000000000	ohm·cm	ASTM D257
Water Absorption	0.21	%	ASTM D570

Regulatory & Compliance

Knowde Enhanced TDS