Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
Arc Resistance | 153 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.1e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 184 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 156 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.054 | — | ASTM D150 |
Flexural Modulus | 7903 | MPa | ASTM D790 |
Flexural Strength | 89.9 | MPa | ASTM D790 |
Heat Resistance | 202 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 89 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.7 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 18.1 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0087 | m/m | ASTM D6289 |
Oxygen Index | 26.9 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.33 | % | ASTM D6289 |
Rockwell Hardness | 79 | E-Scale | ASTM D785 |
Specific Gravity | 1.48 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 8279 | MPa | ASTM D638 |
Tensile Strength | 55 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.44 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 300000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.23 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.68 | g/cm³ | ASTM D1895 |
Arc Resistance | 142 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.1e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 210 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 189 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.2 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.056 | — | ASTM D150 |
Flexural Modulus | 9049 | MPa | ASTM D790 |
Flexural Strength | 98.9 | MPa | ASTM D790 |
Heat Resistance | 205 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 104 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.4 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0053 | m/m | ASTM D6289 |
Oxygen Index | 26.9 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.3 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.2 | % | ASTM D6289 |
Rockwell Hardness | 88 | E-Scale | ASTM D785 |
Specific Gravity | 1.47 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 9180 | MPa | ASTM D638 |
Tensile Strength | 61 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.44 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 710000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.22 | % | ASTM D570 |
Regulatory & Compliance