Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.63 | g/cm³ | ASTM D1895 |
Arc Resistance | 158 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 179 | V | ASTM D3638 |
Compressive Strength | 183 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 169 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.083 | — | ASTM D150 |
Flexural Modulus | 8547 | MPa | ASTM D790 |
Flexural Strength | 89.6 | MPa | ASTM D790 |
Heat Resistance | 203 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 93 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.4 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 17.7 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0082 | m/m | ASTM D6289 |
Oxygen Index | 29.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.2 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.29 | % | ASTM D6289 |
Rockwell Hardness | 107 | E-Scale | ASTM D785 |
Specific Gravity | 1.5 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 9669 | MPa | ASTM D638 |
Tensile Strength | 56 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.49 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 300000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.27 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.64 | g/cm³ | ASTM D1895 |
Arc Resistance | 146 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 182 | V | ASTM D3638 |
Compressive Strength | 211 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 202 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.078 | — | ASTM D150 |
Flexural Modulus | 9540 | MPa | ASTM D790 |
Flexural Strength | 82.3 | MPa | ASTM D790 |
Heat Resistance | 214 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 93 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.4 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.7 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0035 | m/m | ASTM D6289 |
Oxygen Index | 29.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.9 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.2 | % | ASTM D6289 |
Rockwell Hardness | 88 | E scale | ASTM D785 |
Specific Gravity | 1.5 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 9974 | MPa | ASTM D638 |
Tensile Strength | 57 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.49 | W/m/°C | ASTM E1461 |
Volume Resistivity | 1400000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.22 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance