Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Features
- EVA/LDPE copolymer resin film with 8.7% vinyl acetate with thermal stabilizer
- Finish: Taffeta/Matte
- Low-tack paper carrier with no adhesive transfer laminated to matte finish side
Properties
- Physical Form
- Physical Properties
- Mechanical Properties
- Thermal Properties
Value | Units | Test Method / Conditions | |
Thickness (Taffeta Finish) | 3.7 +/- 0.3 | mil | PTM - QA- 005 |
Thickness (Matte Finish) | 2.0 +/- 0.3 | mil | PTM - QA- 005 |
Density | 0.93 | g/cm³ | ASTM - D1505 |
Gloss (at 60°, Matte/Taffeta) | 20.7/14 | GU | ASTM - D2457 |
Transmittance (Film) | 46.0 | % | ASTM - E792 |
Value | Units | Test Method / Conditions | |
Tensile Elongation at Break (MD/TD) | 190/455 | % | ASTM - D882 |
Tensile Strength at Break (MD/TD) | 3820/2425 | psi | ASTM - D882 |
Peel from Film | 11.0 | g/in | ASTM - D3330 Method A |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature | 77.0 | °C | ASTM -D1525 |
Melt Mass -Flow Rate (190°C/2.16kg) | 2.0 | g/10 min | ASTM -D1238 |
Melting Temperature | 100.0 | °C | ASTM -E1356 |
Peak Crystallization Temperature | 85.0 | °C | ASTM -D3418 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Technical Information
- Taffeta finish increases the original film thickness by almost 2 mil thickness. Original film thickness with matte finish is 2.0 +/- 0.3 mil.
Storage & Handling
- Shelf Life
- 1 Year from date of manufacture