Properties
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Processing Properties
- Electrical Properties and Flammability
Value | Units | Test Method / Conditions | |
Tensile Modulus | 8400 | MPa | ISO 527-2 |
Young Modulus | 125 | MPa | ISO 527-2 |
Tensile Strength at Break | 95 | MPa | ISO 527-2 |
Tensile Strength at Yield | 3 | Mpa | ISO 527-2 |
Elongation at Break | 1.5 | % | ISO 527-2 |
Elongation at Yield | 9000 | % | ISO 527-2 |
Flexural Modulus | 155 | Mpa | ISO 178 |
Flexural Strength | 90 | Mpa | ISO 178 |
Izod notched impact (23°C) | 7.5 | kJ/m2 | ISO 180/1A |
Izod notched impact (-30°C) | 6.5 | kJ/m2 | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Density | 1.58 | g/cm3 | ISO 1183 |
Ash Content | 25 | % | ISO 3451 |
Water Absorption (Saturation in water 23°C) | 0.2 | % | ISO 62 |
Water absorption,(Equilibrium value) (50% RH, 23°C) | 0.15 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
MFR/MFI(Melt Flow Rate,250 °C 2,16 kg) | 6 - 8 | g/10 min | ISO 1133 |
HDT A (1.80 Mpa) | 160 | °C | ISO 75-2 |
HDT B (0.45 Mpa) | 155 | °C | ISO 75-2 |
Value | Units | Test Method / Conditions | |
Melting Temperature, DSC | 165 | °C | ISO 11357-1/-3 |
Melt Temperature, for processing | 180-210 | °C | — |
Cylinder Settings | 190-230 | °C | — |
Screw Design | Universal Type | — | — |
Mould Temperature, injection moulding | 80-110 | °C | — |
Moulding shrinkage (parallel,2mm) | 0.4 | % | ISO 294-4 |
Moulding shrinkage (normal,2mm) | 1.6 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | class | UL94 |
Comparative Tracking Index (CTI, 3 mm-Solution A) | 500 | V | IEC 60112 |
Volume Resistivity | 1.00E+14 | Ohm.m | IEC 60093 |
Surface Resistivity | 10000000000000000 | ohm | IEC 60093 |