LNP™ STAT-LOY™ Compound A3000XXP

Identification & Functionality

Additives Included

Anti-Static Agent

Chemical Family

Acrylonitrile Butadiene Styrene (ABS),

Styrenics

Fillers Included

Proprietary

Polymer Name

Acrylonitrile Butadiene Styrene (ABS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Anti-Static,

No Added PFAS,

Unreinforced

Applications & Uses

Markets

Electrical & Electronics,

Industrial

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Electrical/Electronic Applications,

Industrial Applications,

Semiconductor Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.08	g/cm³	ISO 1183
Melt Flow Rate (at 230°C, 5 kgf) ¹¹	19	g/10 min	ASTM D1238
Mold Shrinkage (flow) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	0.6 - 0.8	%	SABIC method
Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹	0.5	%	ISO 62-4
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.2	%	ISO 62-4

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Modulus (at 1 mm/min) ¹¹	1800	MPa	ISO 527
Tensile Stress (Yield, 50 mm/min) ¹¹	40	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	27	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	3.6	%	ISO 527
Tensile Nominal Strain (Break, 50 mm/min) ¹¹	17.9	%	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	1800	MPa	ISO 178
Flexural Strength (at 2 mm/min) ¹¹	56	MPa	ISO 178
Tensile Modulus (at 50 mm/min) ¹¹	1900	MPa	ASTM D638
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	40	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	27	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	3.7	%	ASTM D638
Tensile Nominal Strain (Break, Type I, 50 mm/min) ¹¹	14.6	%	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	1900	MPa	ASTM D790
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	59	MPa	ASTM D790

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	90	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	75	°C	ASTM D648
Vicat Softening Temperature (Rate B/50) ¹¹	94	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	95	°C	ISO 306
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.0001	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.00011	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	92	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	81	°C	ISO 75/Af

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ᵈ ¹¹	10000000000 - 1000000000000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	91	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	1066	J/m	ASTM D4812
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	135	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	12	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	70 - 80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.05 - 0.1	%	—
Melt Temperature ⁷	200 - 210	°C	—
Front - Zone 3 Temperature ⁷	205 - 215	°C	—
Middle - Zone 2 Temperature ⁷	195 - 205	°C	—
Rear - Zone 1 Temperature ⁷	180 - 195	°C	—
Mold Temperature ⁷	10 - 50	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 