Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Characteristics
- Injection Grade
- The most state of the art form US NOVA CHEMICAL
- Low Residual Monomer
- Good Heat Resistance
- Mold Dimension Stability
- Good Transparency
- Easy Processing
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Injection Molding
Value | Units | Test Method / Conditions | |
Elongation at Break (23°C, 1/8” Sample) | 2.0 | % | D638 |
Haze (2.8mm thick) | 0.4 | % | - |
Izod Impact Strength (23°C, A method, notched 1/4”×1/2”×5/2”) | 1.4 | kg-cm/cm | D256 |
Melt Flow Index (200°C, 5 kg load) | 7.0 | g/10min | D1238 |
Residual SM monomer | 300.0 | ppm | - |
Specific Gravity | 1.046 | - | D542 |
Tensile Strength at Yield (23°C,1/8” Sample) | 450.0 | kg/cm2 | D638 |
Vicat Softening Temperature (1 kg load, 3 mm Thick ,120 °C/hr ) | 100.0 | °C | D1525 |
Value | Units | Test Method / Conditions | |
RTI Elec (1.5 mm) | 50.0 | - | UL 746 |
RTI Elec (3.0 mm) | 50.0 | - | UL 746 |
RTI Elec (6.0 mm) | 50.0 | - | UL 746 |
RTI Imp (1.5 mm) | 50.0 | - | UL 746 |
RTI Imp (3.0 mm) | 50.0 | - | UL 746 |
RTI Imp (6.0 mm) | 50.0 | - | UL 746 |
RTI Str (1.5 mm) | 50.0 | - | UL 746 |
RTI Str (3.0 mm) | 50.0 | - | UL 746 |
RTI Str (6.0 mm) | 50.0 | - | UL 746 |
Value | Units | Test Method / Conditions | |
Arc Resistance | PLC 6 | - | ASTM D495 |
Comparative Tracking Index | PLC 1 | - | UL 746 |
High Amp Arc lgnition (1.5 mm) | PLC 3 | - | UL 746 |
High Amp Arc lgnition (3.0 mm) | PLC 3 | - | UL 746 |
High Amp Arc lgnition (6.0 mm) | PLC 3 | - | UL 746 |
High Voltage Arc Tracking Rate | PLC 2 | - | UL 746 |
Hot-Wire Ignition (1.5 mm) | PLC 2 | - | UL 746 |
Hot-Wire Ignition (3.0 mm) | PLC 1 | - | UL 746 |
Hot-Wire Ignition (6.0 mm) | PLC 0 | - | UL 746 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.5 mm, ALL) | HB | - | UL 94 |
Flame Rating (1.5 mm, ALL) | HB75 | - | IEC 60695-11-10, -20 |
Flame Rating (3.0 mm, ALL) | HB | - | UL 94 |
Flame Rating (3.0 mm, ALL) | HB40 | - | EC 60695-11-10, -20 |
Flame Rating (6.0 mm, ALL) | HB | - | UL 94 |
Flame Rating (6.0 mm, ALL) | HB40 | - | IEC 60695-11-10, -20 |
Value | Units | Test Method / Conditions | |
Back Pressure | 71 - 213 | psi(kgf/cm2) | - |
Drying Temperature | 80 - 85 | °C | - |
Drying Time | 2.0 - 4.0 | hr | - |
Front Zone | 205 - 225 | °C | - |
Melt Zone | 180 - 190 | °C | - |
Middle Zone | 195 - 220 | °C | - |
Mold Temperature | 35 - 70 | °C | - |
Molding Pressure | Low to Moderate | - | - |
Molding Speed | Low to Moderate | - | - |
Nozzle | 210 - 230 | °C | - |
Rear Zone | 185 - 210 | °C | - |
Screw Speed | 30 - 120 | rpm | - |
Regulatory & Compliance
- Certifications & Compliance