Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- CASE Ingredients Functions
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Adhesive & Sealant Type
- Plastics & Elastomers End Uses
- Application
(1) Adhesives: Recommended for epoxy, urethane, and rubber adhesives to enhance adhesion to metals, plastics and elastomers. Increased T-peel strength. Improved resistance to moisture, heat and corrosive environments.
(2) Coatings: Recommended for enhancing adhesion of epoxy, urethane, alkyd, acrylic, polyester and other solvent-borne coatings to metal surfaces with resultant reduction in corrosion. Also enhances adhesion to many plastic surfaces. Useful in most water-borne coatings (Latex and polymer dispersion) for enhanced adhesion to metal and plastic substrates.
Properties
- Physical Form
- Physical Properties
Value | Units | Test Method / Conditions | |
Active Matter Content | 50.5 | wt% | — |
Complexed Organics | 18.2 - 18.6 | — | — |
Specific Gravity | 1.39 | g/ml | — |
Total Metal Content | 10.4 - 11.8 | % | — |
pH Value (2% Solution) | 4.15 | — | — |
Organofunctionality | Amino | — | — |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Procedure
HIGH SHEAR MIXING NECESSARY IN ALL SOLVENT-BORNE SYSTEMS
1. Coatings/ Inks: Optimum performance is achieved when added directly to the grind stage resin and high shear mixed for 15 mins before adding other components. Must be high shear mixed with a Cowles type mixer. Milling alone is not sufficient.
- Two component epoxies: Add to resin (A side); level is 0.5 - 1.0 wt% of total binder (combined resin + hardener).
- Two component urethanes: Add to polyol (B side); level is 0.5 - 1.0 wt. per cent of total binder (combined isocyanate +polyol).
2. Adhesives: 0.5 - 1.0 phr, post add recommended under agitation.
3. Plastics: 0.5 - 1.0 phf (parts per hundred filler; recommend pretreat of pigments/ fillers in a Henschel or similar mixer and subsequently compound with resin. For high surface area pigments/ fillers, ie fumed silica, carbon black, phthalo, and similar.
4. Rubber: 0.5 - 1.0 phr, add directly onto silica or other filler and compound in a Banbury mixer.