Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Filler Content
- 10 - 14
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Strength | max. 20 | MPa | ISO 527-2 |
Flexural Strength | max. 28 | MPa | ISO 178 |
Flexural Modulus (23°C) | 1300 | MPa | ISO 178 |
Charpy Unnotched Impact Strength (23°C) | NB | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (-20°C) | 13 | kJ/m² | ISO 179 |
Value | Units | Test Method / Conditions | |
Melt Flow Index - MFI (230°C/2.16kg) | 2 | g/10min | ISO 1133 |
Density | 0.98 | g/cm³ | ISO 1183/A |
Molding Shrinkage - Flow | 1.2 - 1.4 | % | ISO 294-4 |
Molding Shrinkage - Across Flow | 1.2 - 1.4 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature B (120°C/h at 455kPa) | 95 | °C | ISO 75/1 |
Vicat Softening Tempurature A (50°C/h at 9,81N) | 135 | °C | ISO 306 |
Vicat Softening Tempurature B (50°C/h at 49,05N) | 60 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 70 - 80 | °C | - |
Drying Time | 2 - 4 | h | - |
Back Pressure | 60 - 100 | bar | - |
Melt Temperature | 205 - 260 | °C | - |
Mold Temperature | 40 - 80 | °C | - |
Peripherical Screw Speed | 600 - 750 | mm/s | - |