G-BOND 60P 40THC is a 60gsm thermoreactive glass mesh combined with a 40gsm EVA coating. G-BOND is used to stabilize core materials (balsa, PVC, PET).

C-PLY™ SP BX 400 C3,4 50K HS is a 400 gsm biaxial spread-tow carbon NCF, +45°/-45°, 200 gsm/ply.It is made using 50K HS carbon fiber.The heavy-tow carbon fiber spreading process enables the manufacture of homogeneous plies combined using a chain stitch.

DIAGONAP™ DX 4001 is a biaxial glass fabric comprising of two stitched plies. It has a total weight of 828 gsm. This reinforcement is primarily used in the Marine industry.

G-PLY™ BT830 T4 is a biaxial 0°/90° 844 gsm glass NCF. This multiaxial fabric is intended for the Marine industry, primarily for infusion processes but also for HLU processes.

G-PLY™ BX800S C3 is a biaxial +45°/-45° 810 gsm stitched glass NCF. The addition of threads at 0° increases the stablility of this reinforcement. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP BX30 150 C3,4 12K HS is a 150 gsm biaxial spread-tow carbon NCF, +30°/-30°, 75 gsm/ply.It is made using 12K HS carbon fiber.The special orientation at 30° angles and ultra-lightweight plies, reducing the weight of the material, make this suitable for use on composite parts, according to the direction of mechanical stresses.

C-PLY™ SP 0/45 75/75 CT3,4 12K HS is a 150 gsm biaxial spread-tow carbon NCF, 0/+45°, 75 gsm/ply.It is made using 12K HS carbon fiber.The anisotropic orientation ensures that use of the material weight is optimized according to the direction of the forces exerted on the part to be made.

C-PLY BX600 C2,5 50K TRW40 is a 600 gsm biaxialcarbon NCF, +45°/-45°, 300 gsm/ply. It is made using TRW40 multi compatible resin carbon fiber. Plies are combined using a chain stitch. This reinforcement is paricularly adpated to the marine industry or parts which are resin infused.

G-PLY™ BX600S M225 T3 is a biaxial +45°/-45° glass NCF, stitched to a 225gsm mat, resulting in a total weight of 839 gsm. The addition of threads at 0° increases the stablility of this reinforcement. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

G-BOND 52P 25THCM3 is a 52gsm thermoreactive glass mesh combined with a 25 gsm copolyester coating. It is used to stabilize balsa core materials.

DIAGONAP™ DT 20.40.1.01 is a triaxial glass fabric comprising of threestitched plies. It has a total weight of 858 gsm. This reinforcement is primarily used in theMarine industry.

G-PLY™ BX300S C4 is a biaxial +45°/-45° 332 gsm stitched glass NCF. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP BT300 CT3 50K HS is a 300 gsm biaxial spread-tow carbon NCF, 0°/-90°, 150 gsm/ply.It is made using 50K HS carbon fiber.The heavy-tow carbon fiber spreading process enables the manufacture of lightweight plies combined using a hybrid chain/tricot stitch.

G-PLY™ BT583/M450 T6 is a biaxial 0°/90° glass NCF, stitched to a 450gsm mat, resulting in a total weight of 1061 gsm. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP BX 200 C3,4 12K HS is a 200 gsm biaxial spread-tow carbon NCF, +45°/-45°, 100 gsm/ply.It is made using 12K HS carbon fiber.C-PLY™ SP is manufactured using a process to deposit and spread the carbon fibers, and assembled using a functionalized stitch.

C-PLY™ BT600 T2,5 50K TRW40 is a 600 gsm biaxial carbon NCF, 0°/90°, 300 gsm/ply. It is made using TRW40 multi compatible resin carbon fiber. Plies are combined using a tricot stitch. This reinforcement is paricularly adpated to the marine industry or parts which are resin infused.

C-PLY™ SP BX60 150 C3,4 12K HS is a 150 gsm biaxial spread-tow carbon NCF, +60°/-60°, 75 gsm/ply.It is made using 12K HS carbon fiber.The special orientation at 60° angles and ultra-lightweight plies, reducing the weight of the material, make this suitable for use on composite parts, according to the direction of mechanical stresses.

C-PLY™ SP BT600 CT3,4 50K HS is a 600 gsm biaxial spread-tow carbon NCF, 0°/-90°, 300 gsm/ply.It is made using 50K HS carbon fiber.The heavy-tow carbon fiber spreading process enables the manufacture of homogeneous plies combined using a hybrid chain/tricot stitch.

G-PLY™ BX468S T3 is a biaxial +45°/-45° 482 gsm glass NCF. The addition of threads at 0° and 90° increases the stablility of this reinforcement. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP BX 240 T3,3 50K HS is a 240 gsm biaxial spread-tow carbon NCF, +45°/-45°, 120 gsm/ply.It is made using 50K HS carbon fiber.The heavy-tow carbon fiber spreading process enables the manufacture of lightweight plies combined using a tricot stitch to produce a homogeneous reinforcement.

C-PLY™ SP BX100 C3,4 12K HS is a 100 gsm biaxial spread-tow carbon NCF, +45°/-45°, 50 gsm/ply.It is made using 12K HS carbon fiber.The process used to deposit and spread the carbon fibers enables the manufacture of very lightweight plies combined using a functionalized stitch.

C-PLY™ SP BX30 100 C3,4 12K HS is a 100 gsm biaxial spread-tow carbon NCF, +30°/-30°, 50 gsm/ply.It is made using 12K HS carbon fiber.The special orientation at 30° angles and ultra-lightweight plies, reducing the weight of the material, make this suitable for use on composite parts, according to the direction of mechanical stresses.

C-PLY™ SP BT400 CT3,4 50K HS is a 400 gsm biaxial spread-tow carbon NCF, 0°/-90°, 200 gsm/ply.It is made using 50K HS carbon fiber.The heavy-tow carbon fiber spreading process enables the manufacture of homogeneous plies combined using a hybrid chain/tricot stitch.

G-PLY™ Q972 T4 is a quadraxial 0°/+45°/-45°/90° 982 gsm glass NCF. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP BX150 C3,4 12K HS is a 150 gsm biaxial spread-tow carbon NCF, +45°/-45°, 75 gsm/ply.It is made using 12K HS carbon fiber.C-PLY™ SP is manufactured using a process to deposit and spread the carbon fibers, and assembled using a functionalized stitch.

G-PLY™ BX600S T3 is a biaxial +45°/-45° 616 gsm stitched glass NCF. The addition of threads at 0° increases the resistance of this reinforcement. This multiaxial fabric is intended in particular for the shipbuilding industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP TL150 CT3,4 12K HS is a 150 gsm triaxial spread-tow carbon NCF, 0/+45/-45°, 50 gsm/ply.It is made using 12K HS carbon fiber.The carbon fiber spreading process enables the manufacture of ultra-lightweight plies combined using a hybrid chain/tricot stitch.

C-PLY™ SP BX 300 T3,3 50K HS is a 300 gsm biaxial spread-tow carbon NCF, +45°/-45°, 150 gsm/ply.It is made using 50K HS carbon fiber.The heavy-tow carbon fiber spreading process enables the manufacture of lightweight plies combined using a tricot stitch to produce a homogeneous reinforcement.

G-PLY™ Q1201 T4 is a quadraxial 0°/+45°/-45°/90° 1211 gsm glass NCF. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP Q 600 CT3,4 50K HS is a 600 gsm quadriaxial carbon NCF, 0/+45/90/-45°, 150 gsm/ply. It is made using 50K HS carbon fiber. Plies are combined using a hybrid chain/tricot stitch. Applications are numerous, in marine it can replace several stacked reinforcements at +/45 deg and 0/90 deg for process cost improvement.

G-PLY™ TL1236 T3 is a glass NCF triaxial 0°/+45°/-45° of 1246 gsm. This multiaxial fabric is intended in particular for the Marine industry, primarily for infusion processes but also for HLU processes.

C-PLY™ SP 0/-45 75/75 CT3.4 12K HS is a 150 gsm biaxial spread-tow carbon NCF, 0/-45°, 75 gsm/ply.It is made using 12K HS carbon fiber.The anisotropic orientation ensures that use of the material weight is optimized according to the direction of the forces exerted on the part to be made.

C-PLY™ SP BX 600 C3,4 50K HS is a 600 gsm biaxial spread-tow carbon NCF, +45°/-45°, 300 gsm/ply.It is made using 50K HS carbon fiber.The heavy-tow carbon fiber spreading process enables the manufacture of homogeneous plies combined using a chain stitch.

G-BOND 60P 27THC is a 60gsm thermoreactive glass mesh combined with a 25gsm EVA coating. G-BOND is used to stabilize core materials (balsa, PVC, PET).

C-PLY™ SP BX 300 T3,3 24 K HS is a 300 gsm biaxial spread-tow carbon NCF, +45°/-45°, 150 gsm/ply.It is made using 24K HS carbon fiber.The carbon fiber spreading process enables the manufacture of lightweight plies combined using a tricot stitch.

G-BOND 52P 25THCM is a 52gsm thermoreactive glass mesh combined with a 25 gsm copolyester coating. G-BOND is used to stabilize core materials (balsa, PVC, PET).