To simplify your formulation processes, we provide bis GMA already diluted in a 80:20 ratio with TEGDMA. Bis-GMA and triethylene glycol dimethacrylate are commonly paired in dental formulations. All of our bisGMA products carry the lowest levels of BPA or bisphenol A on the market.

PL-7210 has a unique combination of high tensile strength and good elongation, which results in excellent toughness upon curing. PL-7210 is also very low color.

PL-7113 is a non-yellowing urethane that exhibits a high degree of elongation. It also has a high rate of conversion with low average shrinkage stress. PL-7113 can be added to formulations to add toughness.

PL-7021 has a unique structure which results in a flexible cured product. Adding PL-7021 to formulations has been shown to increase toughness.

PL-7110 is a low color urethane that is a viscous liquid at room temperature. Upon cure, PL-7110 creates a tough polymer with percent elongation near 60%. PL-7110 is non-yellowing and can be used in formulations to add toughness.

Bisphenol A Epoxy Methacrylate possesses a fast cure speed that forms a stiff polymer with above average hardness.

BisGMA/Triethyleneglycol Dimethacrylate (70/30)

PL-7121 is a novel low-shrink urethane monomer based on Esstech's proprietary methacrylate technology. PL-7121 possesses a volumetric shrinkage of 2.0 - 2.5% and conversion of 65 - 80% without filler. PL-7121 has very low color and can be added to formulations to add toughness. PL-7121 possess the excellent combination of superior elongation and strength.

PL-7003 is a low viscosity urethane that exhibits very fast cure speeds. Upon curing, PL-7003 exhibits excellent hardness and very low color. PL-7003 can be used in formulations to add strength.

PL-7130 is a low color urethane that is a viscous liquid at room temperature. Upon cure, PL-7130 creates a flexible yet tough polymer with percent elongation near 80%. PL-7130 is non-yellowing and can be used in formulations to add flexibility.

PL-7011 exhibits excellent flexibility upon curing. It is a non-yellowing extended urethane dimethacrylate and can be used in formulations to add toughness.

PL-7013 has a relatively low viscosity but upon curing exhibits high conversion and low shrinkage. It exhibits excellent flexibility once cured. PL-7013 is very low color.

PL-7002 is a tetrafunctional polymethacrylate. This increased functionality results in faster cure speeds due to increased cross-linking capacity. Upon curing, PL-7002 exhibits very high Shore D hardness values. PL-7002 is non-yellowing and can be used in formulations to add strength.

PL-7000 is a low viscosity urethane dimethacrylate. When cured, PL-7000 exhibits good hardness and strength. PL-7000 is low in color.

PL-7100B has a very high conversion rate upon curing, resulting in low shrinkage and a high strength material. PL-7100B is non-yellowing and can be used in formulations to add strength.

PL-7010 is an extended urethane dimethacrylate with a relatively low viscosity. It can be added to formulations to improve flexibility. PL-7010 is low color and non-yellowing upon cure.