Value | Units | Test Method / Conditions | |
Tensile Strength | 140 | MPa | ISO 527 |
Tensile Modulus | 7400 | MPa | ISO 527 |
Flexural Strength | 200 | MPa | ASTM D 790 |
Flexural Modulus | 6300 | MPa | ASTM D 790 |
Charpy Notched Impact Strength (-20°C) | 7 | kJ/m2 | ISO 179/1eA |
Charpy Impact Strength (23°C) | 50 | kJ/m2 | ISO 179/1eU |
Charpy Notched Impact Strength (23°C) | 10 | kJ/m2 | ISO 179/1eA |
Charpy Impact Strength (-20°C) | 27 | kJ/m2 | STN EN ISO 179 |
Elongation | 3 | % | ASTM D638 |
Value | Units | Test Method / Conditions | |
Melt Mass Flow Rate - MFR (230°C/2.16 kg) | 3 | g/10 min | ASTM D1238 |
Density | 1.3 | g/cm3 | ISO 1183/A |
Water Content | 0.15 | % | STN EN ISO 3344 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT | 200 | °C | STN EN ISO 75-2 (A) |
Melting Temperature (DSC) | 220 | °C | STN EN ISO 11357-1 |
Vicat Softening Temperature (B) | 210 | °C | STN EN ISO 306 |
Value | Units | Test Method / Conditions | |
Surface Resistivity | 8.00E+13 | ohm | STN 34 6460 |
Electric Strength | 20 | kV/mm | IEC 60243-1 |
Comparative Tracking Index - CTI (A) | 575 | V | STN EN 60112 |
Volume Resistivity | 500000000000.0 | ohm.m | STN 34 6460 |
Value | Units | Test Method / Conditions | |
Glow Wire Test (3 mm) | 650 | °C | STN EN 60695-2-12 |
Flammability | HB | - | UL 94 |
Value | Units | Test Method / Conditions | |
Mold Temperature Range | 70 - 90 | °C | -- |
Drying: Temperature/Time | 80/04 | °C/h | -- |
Manufacturing Shrinkage - length/width | 0.50/1.38 | % | STN EN ISO 294-4 |
Injection Pressure | 70 - 120 | MPa | -- |
Melt Temperature Range | 250 - 280 | °C | -- |