LNP™ THERMOCOMP™ Compound PX92248

Identification & Functionality

Additives Included

Impact Modifier,

Mold Release Agent,

UV Stabilizer

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyamide 6 (PA 6)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Cost Effective,

Good Mold Release,

Good UV Stability,

Good Weather Stability,

High Ductility,

High Impact Resistance,

High Modulus,

High Stiffness,

Impact Modified,

UV Resistant,

UV Stabilized

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Fishing Lines,

Fishing Nets,

Garden Equipment,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break) ¹¹	107	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	107	MPa	ASTM D638
Tensile Strain (Break) ¹¹	2.5	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.5	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	8840	MPa	ASTM D638
Flexural Stress ¹¹	179	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	179	MPa	ASTM D790
Flexural Modulus ¹¹	7220	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	7220	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.34	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2	%	ASTM D955

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	195	°C	ASTM D648

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	843	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	138	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	265 - 275	°C	—
Front - Zone 3 Temperature ⁷	275 - 290	°C	—
Middle - Zone 2 Temperature ⁷	265 - 275	°C	—
Rear - Zone 1 Temperature ⁷	250 - 260	°C	—
Mold Temperature ⁷	80 - 95	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 