Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.24 | g/cm³ | ISO 1183 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.4 | % | ISO 62-1 |
Specific Gravity ¹¹ | 1.24 | — | ASTM D792 |
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.3 | % | ASTM D570 |
Mold Shrinkage (flow) ᵍ ¹¹ | 0.4 - 0.7 | % | SABIC method |
Value | Units | Test Method / Conditions | |
Tensile Modulus (at 1 mm/min) ¹¹ | 2500 | MPa | ISO 527 |
Tensile Strain (Yield, 50 mm/min) ¹¹ | 5.9 | % | ISO 527 |
Tensile Stress (Break, 50 mm/min) ¹¹ | 60 | MPa | ISO 527 |
Tensile Stress (Yield, 50 mm/min) ¹¹ | 76 | MPa | ISO 527 |
Flexural Modulus (at 2 mm/min) ¹¹ | 2500 | MPa | ISO 178 |
Flexural Stress (Yield, at 2 mm/min) ¹¹ | 115 | MPa | ISO 178 |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 70 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 50 - 100 | % | ASTM D638 |
Tensile Modulus (at 50 mm/min) ¹¹ | 2480 | MPa | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 106 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2690 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 170 | °C | ISO 75/Af |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 183 | °C | ISO 75/Bf |
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000061 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000062 | 1/°C | ISO 11359-2 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 174 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000056 | 1/°C | ASTM D696 |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 160 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 140 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 160 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 3.00E+17 | Ω.cm | ASTM D257 |
Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0007 | — | ASTM D150 |
Dissipation Factor (at at 1 kHz) ¹¹ | 0.001 | — | ASTM D150 |
Dissipation Factor (at at 1 MHz) ¹¹ | 0.006 | — | ASTM D150 |
Comparative Tracking Index (UL, PLC) ¹¹ | 4 | PLC Code | UL 746A |
Hot Wire Ignition (PLC 1) ¹¹ | min. 4.5 | mm | UL 746A |
Hot Wire Ignition (PLC 3) ¹¹ | min. 1.5 | mm | UL 746A |
High Ampere Arc Ignition (PLC 3) ¹¹ | min. 6 | mm | UL 746A |
High Ampere Arc Ignition (PLC 4) ¹¹ | min. 1.5 | mm | UL 746A |
High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
Arc Resistance (Tungsten, PLC) ¹¹ | 7 | PLC Code | ASTM D495 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
Izod Impact (Notched, at 23°C) ¹¹ | 69 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 120 - 150 | °C | — |
Drying Time ⁷ | 4 | Hrs | — |
Maximum Moisture Content ⁷ | 0.05 | % | — |
Melt Temperature ⁷ | 360 - 370 | °C | — |
Front - Zone 3 Temperature ⁷ | 350 - 360 | °C | — |
Middle - Zone 2 Temperature ⁷ | 340 - 350 | °C | — |
Rear - Zone 1 Temperature ⁷ | 325 - 340 | °C | — |
Mold Temperature ⁷ | 150 | °C | — |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | — |
Screw Speed ⁷ | 30 - 60 | rpm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 4.5 | mm | UL 94 |
UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |