- Typical Properties
Value | Units | Test Method / Conditions | |
Density | 1.59 | g/cm3 | ISO 1183-1 |
Water Absorption (immersed in water 24/96h at +23°C) | 0.07, 0.2 | % | - |
Water Absorption (when saturated in air +23°C / 50%RH) | 0.2 | % | ISO 62 |
Water Absorption (when saturated in water +23°C) | 0.8 | - | ISO 62 |
Melting temperature (DSC, +10°C/min) | 170.0 | °C | ISO 11357-1/-3 |
Length Extension Coefficient (23°C - 100°C) | 20.0 | 10^-6 K^-1 | |
Temperature Dependent Deflection (1.8MPa) | 160.0 | °C | ISO 75-1/-2 |
Max. Operating Temperature in Air (Short Time) | 140.0 | °C | - |
Max. Operating Temperature in Air (min 5000/20000h) | 100.0 | °C | - |
Minimum Service Temperature | -20.0 | °C | - |
Flammability (Oxygen Index) | 15.0 | % | ISO 4589-1 /-2 |
Flammability (UL 94, 3/6 mm thickness) | HB/HB | - | - |
Breaking Strength | 51.0 | MPa | ISO 527-1/2 |
Tensile Strength | 51.0 | MPa | ISO 527-1/2 |
Tensile Stress (Yield Strength) | 9.0 | MPa | ISO 527-1/2 |
Tensile Stress (Elongation at Break) | 12.0 | % | ISO 527-1/2 |
Tensile Stress (Traction Module) | 4200.0 | MPa | ISO 527-1/2 |
Compression (compression at 1/2/5% deformation) | 23, 39, 74 | MPa | ISO 604 |
Charpy Impact Test Uncut | 36.0 | kJ/m2 | ISO 179-1 / 1eU |
Charpy Impact Test Scored | 8.0 | kJ/m2 | ISO 179-1 / 1eU |
Cultivation Hardening | 180.0 | N/mm2 | ISO 2039-1 |
Hardness | 90.0 | M Scale | ISO 2039-2 |
Electrical Impact Resistance | 33.0 | kV / mm | IEC 60243-1 |
Volume Resistivity | min. 10E14 | Ohm.cm | IEC 60093 |
Surface Resistivity | min. 10E14 | Ohm | IEC 60093 |
Creep Current Index (CTI) | 600.0 | - | IEC 60112 |