Value | Units | Test Method / Conditions | |
Density | 1.41 | g/cm3 | ISO 1183-1 |
Water Absorption (immersed in water 24/96h at +23°C) | 17, 33 | mg | ISO 62 |
Water Absorption (immersed in water 24/96h at +23°C) | 0.18, 0.36 | % | — |
Water Absorption (when saturated in air +23°C / 50%RH) | 0.2 | % | ISO 62 |
Water Absorption (when saturated in water +23°C) | 0.8 | — | ISO 62 |
Melting temperature (DSC, +10°C/min) | 168.0 | °C | ISO 11357-1/-3 |
Thermal conductivity (23°C) | 0.31 | W / (Km) | — |
Length Extension Coefficient (23°C - 100°C) | 0.000125 | m / (mK) | — |
Temperature Dependent Deflection (1.8MPa) | 100.0 | °C | ISO 75-1/-2 |
Max. Operating Temperature in Air (Short Time) | 140.0 | °C | — |
Max. Operating Temperature in Air (min 5000/20000h) | 115/100 | °C | — |
Minimum Service Temperature | -50.0 | °C | — |
Flammability (Oxygen Index) | 15.0 | % | ISO 4589-1 /-2 |
Flammability (UL 94, 3/6 mm thickness) | HB/HB | — | — |
Breaking Strength | 70.0 | MPa | ISO 527-1/2 |
Tensile Strength | 70.0 | MPa | ISO 527-1/2 |
Tensile Stress (Yield Strength) | 20.0 | MPa | ISO 527-1/2 |
Tensile Stress (Elongation at Break) | 40.0 | % | ISO 527-1/2 |
Tensile Stress (Traction Module) | 3000.0 | % | ISO 527-1/2 |
Compression (compression at 1/2/5% deformation) | 22, 40, 72 | MPa | ISO 604 |
Flexural Strength | 89.0 | MPa | 178.0 |
Flexural Strength (Elongation) | 7.5 | % | 178.0 |
Flexural Strength (Bending Stress) | 68.0 | MPa | 178.0 |
Charpy Impact Test Uncut | 150.0 | kJ/m2 | ISO 179-1 / 1eU |
Charpy Impact Test Scored | 9.0 | kJ/m2 | ISO 179-1 / 1eU |
Cultivation Hardening | 115.0 | N/mm2 | ISO 2039-1 |
Rockwell Hardness | M80 | — | ISO 2039-2 |
Electrical Impact Resistance | 20.0 | kV / mm | IEC 60243-1 |
Volume Resistivity | min. 10E14 | Ohm.cm | IEC 60093 |
Surface Resistivity | min. 10E13 | Ohm | IEC 60093 |
Relative Permittivity (100Hz) | 3.8 | — | IEC 60250 |
Relative Permittivity (1MHz) | 3.8 | — | IEC 60250 |
Electrical Loss Factor Tan δ (100 MHz) | 0.003 | — | IEC 60250 |
Electrical Loss Factor Tan δ (1 MHz) | 0.008 | — | IEC 60250 |
Creep Current Index (CTI) | 600.0 | — | IEC 60112 |