CRACKBOND® V200 HI-MOD is a two-component, moisture insensitive, high strength epoxy healer/sealer deck penetrant, designed to prolong the life of concrete by sealing cracks against moisture and preventing chloride ion intrusion. It may be successfully applied and cured at temperatures between 60°F and 95°F (16°C and 35°C ).

Product Type: Epoxy Coating, Sealer

Compatible Substrates & Surfaces: Concrete

Features: Good Substrate Wetting, High Modulus, High Strength, Low Odor, Low Viscosity, Moisture Resistant

Technical Data SheetSafety Data Sheet
  • TypeDocument Name
View All Documents

Knowde Enhanced TDS

Identification & Functionality

Product Type

Epoxy Coating,

Sealer

Technologies

Ready-to-Use Products

Product Families

Ready-to-Use Products — Paints & Coatings

Primers & Sealers

Features & Benefits

Ready-to-Use Product Features

Good Substrate Wetting,

High Modulus,

High Strength,

Low Odor,

Low Viscosity,

Moisture Resistant

Advantages and Features
  • Excellent bond strength
  • Moisture insensitive
  • High early strength
  • Easy to mix - 2:1 ratio
  • Low viscosity
  • Low odor
  • High modulus
  • Designed for automated pump or hand mix application
  • Made in the USA in accordance with CFR 49 section 50101

Applications & Uses

Markets

Building & Construction

Applications

Building & Construction — Building Materials

Structural Components

Building & Construction — Infrastructure, Roads & Paving

Pavement, Highways, Roads & Bridges

Compatible Substrates & Surfaces

Concrete

Coating Type

2K (2 component) Coating

General Uses & Applications
  • Extends deck life on bridges and structures
  • Seals concrete floors and roadways
  • Preserves airport runways/taxiways
  • Protects columns & beams in splash zones
  • Consolidation of porous & dusting surfaces
  • Serves as a primer or pre-treatment for subsequent epoxy or urethane deck coatings
Installation and Coverage

In order to achieve maximum results, proper installation is imperative. Coverage will vary according to the porosity of the concrete. One gallon mixed epoxy covers approximately 150 ft2 (14 m2) at a 13 mil thickness on smooth finished concrete.

Clean Up

Always wear appropriate personal protective equipment such as safety glasses and gloves. Clean uncured materials from tools and equipment using a mild solvent, such as CRACKBOND® INDUSTRIAL CITRUS CLEANER from Adhesives Technology Corp. Cured material may only be removed mechanically using a sander or grinder. Collect with absorbent material. Flush area with water. Dispose of in accordance with local, state and federal disposal regulations

Limitations and Warnings
  • For professional use only
  • Do not thin with solvents, as this may affect cure and material properties
  • Concrete should be a minimum of 28 days old prior to sealing
  • Do not apply if rain is expected; allow sufficient time for the substrate to dry after rain or other inclement conditions
  • Avoid overspray or mist conditions when applied by sprayer
  • Compressed air equipment must have an oil/air separator
  • Maximum of one flood coat application
  • When used as a primer or pretreatment prior to overlay, consult ATC representative
  • Placement not to exceed recommended temperature as outgassing may occur - see Mix Instructions
Cure Schedule
Temperature
°F (°C)		 Cure Time
62 (17) 10 hr
67 (19) 9 hr
72 (22) 7 hr
77 (25) 6 hr
82 (28) 5.5 hr
85 (29) 4.5 hr

Properties

Typical Properties
ValueUnitsTest Method / Conditions
Bond Strength Fresh to Hardened Concrete (14 day, 75°F)1,280 (8.8)psi (MPa)C882
Bond Strength Hardened to Hardened Concrete (14 day, 75°F)1,600 (11.0)psi (MPa)C882
Bond Strength Hardened to Hardened Concrete (2 day, 75°F)1,450 (10.0)psi (MPa)C882
Compressive Modulus (7 day, 60°F)240,700 (1,660)psi (MPa)D695
Compressive Yield Strength (7 day, 60°F)8,280 (57.1)psi (MPa)D695
Consistency or Viscosity (60°F)194.0cPC881
Gel Time - 60 Gram Mass (60°F)36.0minC881
Heat Deflection Temperature (7 day, 60°F)125 (51.7)°F (°C)D648
Linear Coefficient of Shrinkage (60°F)0.0001%D2566
Tack Free Cure Time [(30 mil Thin Film), 65°F]6.0hrD2377
Tensile Elongation (7 day, 75°F)6.0%D638
Tensile Strength (7 day, 60°F)5,840 (40.3)psi (MPa)D638
Water Absorption (14 day, 75°F)0.72%D570

Regulatory & Compliance

Standards and Approvals
  • AASHTO M235/ASTM C881-15
  • Type I Grade 1 Class C

Technical Details & Test Data

Specification

The epoxy healer/sealer shall be a two component, 2:1 mix ratio epoxy system supplied in premeasured containers. At 14 days and temperature of 60°F (16°C), the healer/sealer shall have a bond strength of 1,600 psi (11.0 MPa) per ASTM C882. The healer/sealer shall be CRACKBOND V200 HI-MOD from Adhesives Technology Corp., Pompano Beach, Florida.

Packaging & Availability

Availability

Adhesives Technology Corp. (ATC) products are available online and through select distributors providing all your construction needs.

Packaging
Package Size 3 Gallon Kit1
(11 L)		 15 Gallon Kit2
(57 L)

165 Gallon Kit2
(625 L)
Part # B3G-V200 B5G-V200-A
B5G-V200-B		 B55G-V200-A
B55G-V200-B
Pallet Qty. 36 Kits 12 Kits 1 Kit
Pallet Weight (lb.) 1,141 1,743 1,593

Storage & Handling

Storage and Shelf Life

For best results, store between 50°F (10°C) and 95°F (35°C). Shelf life is 24 months when stored in unopened containers in dry conditions.