- Excellent clarity and gloss
- Excellent hot tack
- The treated surface is receptive to inks and adhesives
- Excellent machinability on packaging lines
- aminating substrate applications
- Printing: flexo, rotogravure, reverse printing in laminates
- Direct food packaging (e.g. pasta, bakery, etc.)
- Jumbo packs (e.g. snack food, diapers, etc.)
- Flower wrapping
- Board lamination (lamination of stationery items, documents and playing cards)
- Process
- Cast Film Extrusion Process
- CPP Amination Grade Film
Properties
- Color
- Typical Properties
Value | Units | Test Method / Conditions | |
Coefficient of Friction (Dynamic Film) | 0.3 | — | ASTM D 1894 |
Density | 44.0 | g/cm^3 | ASTMD 1505 |
Gloss (45°C) | 80.0 | N/25.4 mm | ASTM D-2457 |
Nominal Thickness | 25.0 | µm | SH |
O.TR. (23°C & 90%RH) | 3600.0 | ccm2/day | ASTM D 3985 |
Sealing Range | 120 - 140 | °C | SH |
Shrinkage | 45.0 | % | ASTMD 1204 |
Weight (per unit of area) | 22.7 | g/m^2 | ASTMD 1505 |
Wettability (min Treatment level) | 120.0 | mN/m | ISO 8296 |
WVTR (38°C / 90% RH) | 675.0 | g/md | ASTM 1249 |
Yield | 55.0 | m^2/kg | SH |
Tensile Strength | min. 40 | MPa | — |
Elongation at Break | min. 550 | % | ASTM D 882 |
Storage & Handling
- Storage
All films should be stored in a dry environment at a temperature under 30° C. If properly stored, the film will maintain consistent performance over a period of up to 6 months from the date of production and should be converted prior to this time. A prolonged period of storage may cause problems of thickness profile and blocking on account of the elastic memory of thermoplastic film. It is a fact that polypropylene films age with time and will exhibit deterioration in the wetting tension levels. For this reason it is recommended that film stocks are evaluated for ink adhesion prior to printing and if necessary retreated during conversion process to ensure optimal adhesion or inks and adhesives. It is also advisable to allow the film to reach room temperature at least 24 hours prior to use. Sealing9 properties of film deteriorate when corona treatment is present. Aways check the treated side when using the film.