Andur 9500 APLF is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 95 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 9500 APLF with polyols and their combination with Curene 442 and other diamines, or by the use of plasticizers.

Andur 9500 AP/Curene® 442 is a Polyurethane (Polyether, TDI) (PUR-Ether/TDI) product. It is available in North America.

Andur 9-APF-LM is a polyester based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 89 to 92 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.

Andur 7501 DPLF is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer containing .1% or less free TDI. An elastomer with a hardness of 74 to 77 Shore D is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.

Andur 8 APLM is a polyester based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 79 to 82 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various poyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.

Andur 1-75 DP is a polyether based liquid isocyanate-terminated prepolymer. An elastomer with a hardness of 73-77 Shore D is obtained when this prepolymer is cured with Curene 442 [4,4'- methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442 and other diamines, and by the use of plasticizers.

Andur 1-95AP is a polyether (PTMG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 95 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 1-95AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.

Andur 9500 APLF is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 95 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 9500 APLF with polyols and their combination with Curene 442 and other diamines, or by the use of plasticizers.

Andur 7-3 APLF is a polyester based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 70-75 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442, other diamines or through the use of plasticizers.

Andur 2-90AP is a polyether (PTMG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 90 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 2-90AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.

Andur 9002-APTF is a low viscosity liquid prepolymer which can be processed and cured at room temperature with Curene 107 using Oleic acid catalyst to yield an elastomer with a hardness of 88 to 90 Shore A. This system has been specifically formulated to yield a tack-free film in about 60 minutes when catalyzed to a 6 to 8 minute pot life.Andur 9002-APTF is recommended where room temperature processing and curing is desired and a tack-free film within about 60 minutes. If an application does not require a tack-free film, then we recommend using Andur RT 9002 AP.

Andur M-95 AS is a custom formulated MDI based polyurethane elastomer system. It is designed as a low cost, easily processed candidate for use in dunnage applications. M-95 AS is a two component, 1:1 ratio (weight) system that can be processed at room temperature and yields a 95 Shore A elastomer. The system needs no post cure and contains no TDI.