- Fabric Specifications
TK0750 - 750gm Warp Triaxial E-Glass Layer Orientation degrees (°) 0 +45 90 -45 Layer Weight (gm/m2) 354 203 6 203 Material E-Glass E-Glass E-Glass E-Glass Weight, knitting yarn (gm/m²) 8 Material PES Total weight (gm/m²) 774±3% Standard roll width (mm) 1270 - Fabric Specifications
TK1150 - 1150gm Warp Triaxial E-Glass Layer Orientation degrees (°) 0 +45 90 -45 Layer Weight (gm/m2) 413 375 6 375 Material E-Glass E-Glass E-Glass E-Glass Weight, knitting yarn (gm/m²) 10 Material PES Total weight (gm/m²) 1179±3% Standard roll width (mm) 1270 - Typical Laminate Properties
TYPICAL LAMINATE PROPERTIES
Laminate thickness 0.114 per 100gm/m2 Fiber Fraction 50% by weightTest Method 0o +45o 90o -45o Tensile Strength ISO 3268 227 MPa 189 MPa 37* MPa 184 MPa Tensile Modulus ISO 3268 17,240 MPa 14,600 MPa 8,650 MPa 14,100 MPa Compressive Strength BS 2782 182 MPa 147 MPa 147 MPa Compressive Modulus BS 2782 14,500 MPa 14,600 MPa 11,300MPa Flexural Strength 365 MPa Shear Strength, in plane ASTM 4255-83 76 MPa 87 MPa 58 MPa 87 MPa Shear Strength, interlamina BS 2782 36.5 MPa 25.9 MPa 18.7 MPa 25.8 MPa Elongation at break 2.4% 2.4 % 2.9% 2.4 % - Standard Stock
Order Code Description Roll Width Roll Length TK0750 750gm Triaxial E/Glass, tapered 1.27 m 40.7 Lm TK1150 1150gm Triaxial E/Glass, tapered 1.27 m 26.7 Lm